箱式发泡工艺植物纤文基PU泡沫材料研究 摘要：本文以含植物纤文基聚醚多元醇为主要基体树脂，采用箱式发泡工艺制备聚氨酯泡
沫材料。系统研究了树脂种类(植物聚醚多元醇、对苯聚酯多元醇、403聚醚多元醇)、复
配比例、助剂种类和用量、交联剂甘油用量等对聚氨酯泡沫材料性能的影响。研究结果表
明，得到最优配比的各项性能为：压缩强度为 153.40 k Pa、冲击强度为 293.07 kJ·m-2
， 弯
曲强度为 0.10 N/mm2
。玻璃化转变温度为 197.7℃，氧指数为27，符合 B2级阻燃材料标
准。
关键词：植物纤文；多元醇；聚氨酯；泡沫塑料；性能
The Research for Plant Fiber based
Polyurethane Foam
Abstract:With the poly-ether polyols made from plant fiber as the main matrix resin,
polyurethane foams are fabricated by using box-type foam. The influences on polyurethane
foam properties, such as varieties of matrix resin (plant poly-ether polyol, the benzene polyester
polyol, 403 polyethylene polyol),compound ratio, catalyst type and its amount and the amount
of glycerol have been studied on the system. The results show that the optimal ratio of the
impact strength is 293.07 kJ·m-2 ,the compressive strength is 153.40 k Pa, the bending strength
is 0.10 N/mm2.The glass transition temperature is197.7 ℃, the oxygen index is 26.5 to comply
with B2 level flame retardant material standards.
KeyWords: Plant fiber;Polyols; Polyurethane; Foam; Performance
目 录
1 文献综述.1
1.1 聚氨酯简介 1
1.1.1 聚氨酯的结构.1
1.1.2 聚氨酯的性能 1
1.1.3 聚氨酯的用途 2
1.2 聚氨酯泡沫塑料（PUF） 2
1.2.1 硬质聚氨酯泡沫塑料 2
1.2.2 软质聚氨酯泡沫塑料 3
1.3 植物聚醚多元醇概述. 3
1.3.1 植物纤文的基本组成与种类3
1.3.2 植物纤文液化技术研究进展5
1.3.3 植物油基聚醚多元醇. 7
1.3.4 植物纤文基聚醚多元醇. 7
1.3.5 植物纤文聚醚多元醇在聚氨酯中的应用.7
1.4现有问题. 8
1.5选题依据. 8
1.6立选题的意义和目的 8
1.7 研究内容 9
1.8本课题创新点. 9
2 实验部分.10
2.1 实验原料及仪器设备. 10
2.1.1 实验原料及来源 10
2.1.2 仪器设备10
2.2实验方法. 11
植物纤文基聚氨酯泡沫的制备.11
2.3 分析表征 12
2.3.1 表观密度12
2.3.2 弯曲性能13
2.3.3 压缩性能14
2.3.4 冲击性能15
2.3.5 热力学性能16
2.3.6 阻燃性能17
3 结果与讨论. 18
3.1植物纤文基 PU泡沫组合料A 料配方的研究18
3.1.1 基体树脂配比. 18
3.1.2 催化剂用量20
3.1.3 甘油用量21
3.1.4 阻燃剂的最低用量 23
3.1.5 小结. 23
3.2 植物纤文基PU泡沫 AB 料配比的研究24
3.2.1 目视法观察泡孔结构. 24
3.2.2 表观密度25
3.2.3 力学性能25
3.2.4 尺寸稳定性.26
3.2.5 热力学分析27
3.2.6 小结. 27
4 结论.28
4.1 植物聚醚PU泡沫材料的 A 料配方 28
4.2 植物聚醚PU泡沫材料的 AB 料配比. 28
4.3 植物聚醚PU泡沫材料的优化配方.29
致 谢 31
参考文献.32，3586