稀土磷酸盐发光材料的形貌控制及性能研究(2)

时间:2018-05-23 11:32来源:毕业论文
1. RePO4 materials were fabricated by solvothermal method, 180℃,using phosphate as phosphorus source, which change reaction time 12h~24h. The samples were characterized by X-ray Diffractomer and t


1.    RePO4 materials were fabricated by solvothermal method, 180℃,using phosphate as phosphorus source, which change reaction time 12h~24h. The samples were characterized by X-ray Diffractomer and transmission electron microscope. According to the sample topography choose the best optimum reaction time.
2.    RePO4 materials were fabricated by solvothermal method, 180℃,using phosphate as phosphorus source. Using La, Y as the rare earth ion source separately, changing the type of solvent and the ratio of reaction to prepare phosphate. The samples were characterized by X-ray Diffractomer and transmission electron microscope.
3.    The luminescence characteristics of Eu3+ and Tb3+, when it doped in LaPO4 or YPO4, were analyzed Luminescent properties.
Key Words: Rare earth phosphates; Phosphate; Solvothermal method; Fluorescent material
目录
1. 绪论    2
1.1    引言    2
1.2 无机固体发光原理    2
1.2.1 无机固体发光与晶体结构    2
1.2.2 无机固体发光过程    3
1.3 稀土发光材料    3
1.3.1 稀土发光材料的发展    3
1.3.2 稀土发光材料的发光原理    3
1.3.3 稀土发光材料的分类    4
1.3.4 稀土发光材料的优点    4
1.3.5 稀土发光材料的合成方法    5
1.4 稀土磷酸盐    5
1.4.1 稀土磷酸盐的结构    5
1.4.2 稀土磷酸盐发光材料的研究现状    7
1.5 本文研究的目的和意义    9
2    实验部分    11
2.1 试剂和仪器    11
2.2 实验步骤    12
3    实验结果及讨论    13
3.1 水热法合成磷酸钇    13
3.1.1 不同反应时间下制得磷酸钇    13
3.1.2 通过不同P:Y比下改变溶剂配比控制磷酸钇形貌    14
3.1.2.1 Y:P=2:2    15
3.1.2.2 Y:P=2:4    17
3.1.2.3 Y:P=2:6    19
3.1.2.4 Y:P=2:8    21
3.1.2.5 Y:P=2:10    23
3.1.3 改变PH水热合成YPO4    25
3.2 改变稀土离子与P的摩尔比(RE=Y,La,Gd),水热法合成磷酸盐    27
3.2.1 改变Y:P水热法合成磷酸钇    27
3.2.2 改变La:P,水热法合成磷酸镧    29
3.2.3 改变Gd:P,水热法合成磷酸钆    31
3.2.4 YPO4、LaPO4和GdPO4对比    33
3.3    发光性能    34
3.3.1 改变硝酸铕的量    34
3.3.2 改变硝酸铽的量    35
3.3.3同时掺杂铕和铽    37
3.3.4 不同基质下相同发光中心强度比较    38
4    结果及展望    41
参考文献    43
致 谢    45
1. 绪论
1.1    引言
稀土发光材料即为:稀土元素用于发光(荧光)材料的基质成分或是用作激活剂、共激活剂、敏化剂或掺杂剂所制成的发光材料[1]。一般来讲统称为稀土发光材料或稀土荧光材料。稀土元素在发光材料的研究与应用当中占有举足轻重的地位,稀土材料因其自身优异的反应性能,在某些领域具有不可替代的重要作用,因此稀土发光材料已经逐渐取代部分的非稀土发光材料。目前,彩色阴级射线管用的红粉、三基色荧光灯用的蓝粉、绿粉和红粉,等离子显示屏用的红粉、蓝粉,投影电视用的绿粉和三基色粉,都是稀土荧光粉[2]。由此可见,稀土发光材料已经成为信息显示和高效照明器具的关键基础材料之一。 稀土磷酸盐发光材料的形貌控制及性能研究(2):http://www.751com.cn/huaxue/lunwen_16174.html