摘要： 由于传统751价铬钝化工艺对环境污染严重，处理过的产品外观不佳，因此需开发新的防变色工艺。本文采用有机防变色剂对酸性镀镍层表面进行处理，得到一种防变色膜来保护镀镍层。通过改变防变色处理液中饱和长链脂肪酸种类，调节不同的pH值和处理时间来对试样进行处理，以探究最佳防变色工艺。通过塔菲尔极化曲线测试和交流阻抗测试来对防变色处理效果进行评价。最终得出酸性化学镀镍层的防变色液最佳工艺为：月桂酸 1g/L,过氧化苯甲酰0.02g/L，乙醇为溶剂，pH≈8.5，15min，室温条件下。23703
毕业论文关键词：酸性化学镀镍；防变色；交流阻抗；过氧化苯甲酰。
Prevent discoloration of acidic electroless nickel plating layer
Abstract: As traditional hexavalent and trivalent chromium passivation passivation process on environmental pollution, poor appearance of the treated products, the need to develop new anti-discoloration process. In this paper, the organic acid anti-discoloration agent, a nickel plating layer on the surface treatment, to obtain a color proof film. By changing the treatment liquid saturated long chain fatty acid species, and adjusting the pH of the different processing time to process the samples. To evaluate the effect of anti-color processing by Tafel polarization curves and electrochemical impedance testing. Anti-final draw optimum color liquid acidic electroless nickel layer is: lauric acid 1g / L, benzoyl peroxide 0.02g / L, ethanol as solvent, pH ≈ 8.5,15 min, at room temperature.
Key words: Acidic electroless nickel plating; antitarnish; alternating current impedance; benzoyl peroxide。
目录
酸性化学镀镍层的防变色处理 1
1 绪论 1
1.1化学镀镍 1
1.1.1化学镀镍定义 1
1.1.2化学镀镍的机理 1
1.1. 3化学镀镍的发展与应用 2
1.1.4化学镀镍的优点 2
1.1.5 化学镀镍的优点 5
1.2化学镀镍的防变色处理 5
2 实验部分 7
2.1 实验的设备 7
2.2 实验溶液配方 7
2.2.1 除油液 7
2.2.2 除锈液 7
2.2.3 活化液 7
2.2.4 抛光液 7
2.2.5 酸性化学镀镍液 7
2.2.6 有机防变色液 8
2.2.7 对照钝化液 8
2.3 试样的制备 8
2.4 探究方法 9
2.4.1 交流阻抗测试 9
2.4.2极化曲线测试 9
3 实验结果与讨论 11
3.1 结果与分析 11
3.1.1不同PH值下，防变色效果评价 11
3.1.2饱和长链脂肪酸种类的影响 19
3.1.3处理时间的影响 21
3.2 结论 23
致谢 25
参考文献 26
酸性化学镀镍层的防变色处理
1 绪论
化学镀镍层具有较好的抗拉强度、耐磨性、延展性、韧性和抗腐蚀性，广泛应用于机械、电子及轻工业[1]。当下人类正面临着日益严重的环境危机，化学镀镍工艺及相关产业，在为人类的经济生活中作出重要贡献的同时，也在生产活动中不断排放出大量有毒物质，给环境和人类的健康带来一定的危害。
1.1化学镀镍
1.1.1化学镀镍定义
化学镀镍也称为无电解镀镍，是一种不使用外电源，而是利用还原剂使溶液中的金属离子在基体表面还原沉积了金属镀层的成膜技术。原理是金属盐和还原剂在镀液中进行氧化还原反应。 酸性化学镀镍层的防变色处理:http://www.751com.cn/huaxue/lunwen_16895.html