摘要：本文在质量分数为5%的稀硫酸溶液中于不同温度下添加不同浓度的碘离子，采用失重法和动电位极化曲线法，研究了碘离子对低碳钢耐腐蚀性能的影响。通过研究所得实验数据表明，在温度相同的情况下，碘离子对低碳钢的缓蚀效率随着5%稀硫酸中碘离子浓度的升高而增大；而在含有相同浓度碘离子的5%稀硫酸溶液中，随着温度的升高，碘离子对低碳钢的缓蚀效果变差。经过对实验数据的分析与讨论得出。在20℃的温度下，添加70ppm碘离子对低碳钢的缓蚀效果最好。24127
毕业论文关键词： 低碳钢；碘离子；缓蚀剂；极化曲线
Study on corrosion of low-carbon steel in sulfuric acid solution contained iodide ions
Abstract：In this paper, the mass fraction of 5% sulfuric acid solution at different temperatures by adding different concentrations of iodide ions, using the weight loss method and potentiometric polarization curves, the effect of iodide ions on the corrosion resistance of low-carbon steel. Experimental data obtained show Institute, at the same temperature, the inhibition efficiency of the iodide ion along with the low carbon concentration in 5% sulfuric acid increased with increasing iodide ion; while containing the same concentration of iodide ion 5 % dilute sulfuric acid solution, as the temperature rises, the effect of iodide ions on the corrosion of mild steel worse. After analysis and discussion of the experimental data obtained. At 20, adding 70ppm iodine ions on mild steel corrosion best.
Key word: mild steel, sulfuric acid, corrosion inhibitor, adsorption
目 录
1. 绪论 1
1.1 缓蚀剂的概述 1
1.1.1 缓蚀剂的分类 1
1.2 本课题研究的目的和意义 3
1.3缓蚀剂的国内外研究进展 3
2. 金属腐蚀概论 5
2.1金属腐蚀的分类 5
2.2金属防腐蚀的方法 5
2.2.1耐蚀合金防腐蚀 5
2.2.2介质防腐蚀 6
2.3缓蚀剂的防腐蚀原理 7
2.3.1缓蚀剂的电化学原理 7
2.3.2缓蚀剂防腐蚀的物理化学机理 7
3.2.3缓蚀剂研究的方法 9
3. 实验内容 10
3.1实验仪器和试剂 10
3.2本实验的研究方法 10
3.2.1失重法 11
3.2.2电化学法（极化曲线） 11
4. 实验数据的分析与讨论 12
4.1失重法研究碘离子在5%稀硫酸溶液中对低碳钢耐腐蚀性的影响 12
4.1.1失重法 12
4.1.2实验部分 12
4.1.3实验结果与分析 13
4.2电化学法研究碘离子在5%稀硫酸溶液中对低碳钢耐腐蚀性的影响 15
4.2.1 极化曲线外延法 15
4.2.2实验部分 16
4.2.3 实验结果与分析 17
结论 26
致谢 27
参考文献 28
1. 绪论
1.1 缓蚀剂的概述
缓蚀剂是在环境（介质）中以适当的浓度和形式，防止或减缓金属材料腐蚀的一类化学物质或复合物，所以缓蚀剂也可以被称为腐蚀抑制剂。缓蚀剂的用量一般很小，通常在0.1％～1％之间，但是缓释效果十分显著。这种利用缓蚀剂保护金属的方法通常称缓蚀剂保护。缓蚀剂大多数用于中性介质（锅炉用水、循环冷却水）防腐蚀、酸性介质（除锅垢的盐酸，电镀前镀件除锈用的酸溶液）防腐蚀和气体介质（气相缓蚀剂）防腐蚀中。
1.1.1 缓蚀剂的分类 酸性条件下碘离子对低碳钢耐腐蚀性的研究:http://www.751com.cn/huaxue/lunwen_17484.html