摘要化学镀作为制备金属包覆非金属复合粉体的方法之一，其优点是在任何基体如玻璃、陶瓷、塑料或金属表面都能制备出均匀金属镀层。它是基于在水溶液中可控的自催化氧化还原反应，不需要提供电流，对基体没有形状和类型的限制。25831
本文通过对粉体碳酸钙的镀锌技术的研究，从而对烟幕材料的制备工艺与应用形成感性认识，研究粉体颗粒的镀涂原理，并进行测试，研究冷烟材料在遮蔽烟幕方面的应用。
本文主要的研究内容包括对粉体碳酸钙化学镀锌的理论研究，工艺研究以及复合材料的性能测试。
关键词：化学镀 碳酸钙 烟幕遮蔽
毕业论文设计说明书外文摘要
Title Smoke Material Process of zinc-coated calcium carbonate powder formed by electroless plating method.
Abstract
Electroless planting is one of the method to prepare metal-coated non-metallic composite powder, whose advantage is that any substrate such as glass, ceramics, plastic or metal surface can be prepared a uniform metal coating. It is based on a principle that self-catalytic oxidation-reduction reaction can be controlled in aqueous solution. This method does not require the applied current, and there is no restriction on the shape and type of substrate.
This essay studied plated coating powder particles principle, on a basis of calcium carbonate powder galvanizing technology, material preparation and application of smoke forming perceptual, and tested measurement, had a research on cold smoke smokescreen masking material terms Applications.
The main contents of this paper include calcium carbonate powder chemical galvanizing theoretical research, technology research and performance testing of composite materials.
Keywords electroless planting calcium carbonate smoke screening
目 次
1 引言 1
1.1 粉体化学镀的概念 1
1.2 粉体化学镀的研究背景及现状 1
1.3 影响粉体化学镀的因素 2
2 粉体表面改性 3
2.1 表面改性剂及其配方 3
2.2 表面改性方法 3
2.3 表面改性工艺 4
3 碳酸钙改性 5
3.1 概述 5
3.2 碳酸钙粉体表面改性的机理 5
3.3偶联剂对碳酸钙的表面改性 6
3.4 硅烷偶联剂对碳酸钙的表面改性 6
4 硅烷偶联剂水解研究 7
4.1研究背景 7
4.2 硅烷偶联剂的结构与性质 7
4.3 硅烷偶联剂作用机理 7
5 实验内容与方法 9
5.1 前言 9
5.2 实验设备与药剂 9
5.3 实验操作及流程 10
5.4 偶联过程 11
5.5 化学镀银、锌 12
5.6 烟幕实验操作 13
6 实验分析与探讨 14
6.1 影响碳酸钙表面羟基连接的因素 14
6.2 对氢氧化钠处理碳酸钙产物的研究 14
6.3 FT-IR红外光谱分析 15
6.4 X射线衍射分析（XRD） 15
结 论 17
致 谢 18 碳酸钙粉体化学镀锌烟幕材料的工艺研究:http://www.751com.cn/huaxue/lunwen_19792.html