摘要：本文主要对环保型阴离子交换树脂制备过程中的胺化工艺进行了研究。本文运用了无致癌毒性的氯甲基烷基醚对交联聚苯乙烯微球进行氯甲基化，得到的环保型氯球经进一步胺化后，得到环保型阴离子交换树脂,并对其通过傅里叶红外仪对产物的结构进行了表征。本文探讨了环保型氯球的胺化反应过程中各种因素对胺化反应结果的影响规律，确定了最佳的反应条件、反应配方和反应体系。得到最高交换容量为2.76mmol/g，含水量在12%~36%，胺化程度在0.07~0.65的淡黄色透明环保型阴离子交换树脂。34422
毕业论文关键词：胺化反应，阴离子交换树脂，离子交换容量，环保型氯球，三甲胺
Preparation of environmentally friendly anion exchange resin
Abstract:The conditions of amination reaction in the preparation of environmentally friendly anion exchange resin have been studied. In the preparation of environmentally friendly anion exchange resin, the PS-DVB copolymers were chloromethylated with long chain alkylhalomethyl ethers without carcinogenic toxictiy, then the products were aminated and the final products’ structrue were identified by FT-IR. Various factors of amination reaction were studied to obtain the optimal reaction conditions. The results show that the optimal ino-exchange capacity（IEC） reached 2.76mmol/g, water content is 12%~36% and amination degree is 0.07~0.65 ,the light yellow transparent environment-friendly anion exchange resin were obtained.
Keywords:Amination ,Anion exchange resin,Ion exchange capacity,Chlorine methylation cross-linked polystyrene,Tertiary amine
目 录
1绪论 1
1.1 离子交换树脂的概述 1
1.1.1 离子交换树脂的分类 1
1.1.2 离子交换树脂的物理性能 2
1.1.3 离子交换树脂的交换过程 3
1.2 阴离子交换树脂的概述 4
1.2.1 阴离子交换树脂的制备方法 4
1.2.2 阴离子交换树脂的应用领域 5
1.2.3 阴离子交换树脂的发展状况 5
1.3 研究目的和意义 6
2 试验 7
2.1 试剂与仪器 7
2.1.1 原料 7
2.1.2 仪器与设备 7
2.2 交联聚苯乙烯微球的氯甲基化制备 8
2.2.1 交联聚苯乙烯微球的氯甲基化原理 8
2.2.2 交联聚苯乙烯微球的氯甲基化步骤 9
2.3 氯球的胺化 10
2.3.1 氯球的胺化原理 10
2.3.2 氯球的胺化步骤 11
2.4 阴离子交换树脂的性能测定 12
2.4.1 离子交换容量的测定 12
2.4.2 含水量的测定 13
2.4.3 红外谱图的测定 14
2.4.4 胺化程度的测定 14
3 结果与讨论 15
3.1 胺化反应体系的选择 15
3.1.1 溶剂种类对胺化结果的影响 15
3.1.2 胺化试剂种类对胺化结果的影响 16
3.1.3 PH值对胺化结果的影响 16
3.1.4 氯化钠浓度对胺化结果的影响 18
3.2 胺化反应条件的研究 18
3.2.1 反应时间对胺化结果的影响 18
3.2.2 反应温度对胺化结果的影响 19
3.3 胺化反应配方的研究 20
3.3.1 三甲胺用量对胺化结果的影响 20
3.3.2 三甲胺质量分数对胺化结果的影响 21
3.3.3 溶剂用量对胺化结果的影响 22 环保型阴离子交换树脂的制备:http://www.751com.cn/huaxue/lunwen_31917.html