摘要：本论文就一种应用于导电油墨中的金属聚合物复合胶体复合胶体的制备方法进行研究。导电性油墨是指印刷在非导电承印物上，使之具有传导电流和排除积累静电荷能力的油墨，一般是印在塑料、玻璃、陶瓷或纸板等非导电承印物上。本论文将新配制的银氨溶液中加入稳定剂，利用稳定剂的吸附作用，使得反应过程中的银颗粒减少聚集，从而达到了减小银颗粒直径的目的，另外，通过对温度、搅拌、配比等条件的控制制取最合理的金属聚合物复合胶体胶体，制得的金属聚合物复合胶体复合胶体解决了现有技术对设备要求高，对环境污染大的难题。6084
关键词： 金属聚合物复合胶体；复合胶体；导电油墨
Metal-polymer composite colloids research
Abstract: This thesis is a preparation method of metal polymer composite gel applied to a conductive ink. Conductive ink is printed on the non-conductive substrate, the conduction current and eliminate the accumulation of electrostatic charge capacity of the ink, usually printed on plastic, glass, ceramic or cardboard, non-conductive substrate. This paper will join the stabilizer of silver ammonia solution new prepared, using adsorption stabilizer, the silver particles in the reaction process to reduce the aggregation, so as to achieve the purpose of reducing silver particle diameter, in addition, the temperature control, mixing, preparing ratio conditions the metal colloidal polymer science, polymer metal composite gel the prepared solves high reΩuirements for eΩui/minent, the problem of environmental pollution.
Keyword：Metal polymer; Composite gel;electrically conductive in
目 录
1 绪论 1
1.1 选题目的及意义 1
1.2 导电油墨的作用机理 2
1.2.1 渗流作用 2
1.2.2 隧道效应 2
1.2.3 场致发射原理 2
1.2.4 复合导电油墨的导电机理 2
1.3 导电油墨的概况 3
1.4 复合导电油墨的制备技术 4
1.4.1 银浆油墨 4
1.4.2 铜浆油墨 5
1.4.3 碳浆油墨 5
1.4.4 其它制备方法 6
1.5 纳米银离子的制备方法 6
1.5.1 化学还原法 6
1.5.2 微乳液法 7
1.5.3 光化学法 7
1.5.4 电化学法 8
1.5.5 超声波还原法 8
1.5.6 溶胶—凝胶法 8
1.5.7 液相激光烧蚀法 8
2 实验部分 10
2.1 导电油墨的原料 10
2.1.1粘结料 10
2.1.2 溶剂 10
2.1.3 填料 10
2.1.4 助剂 11
2.2实验原理 11
2.3 纳米银的表征 12
2.3.1 纳米材料的表征技术 12
2.3.2 尺寸和形貌（SEM）表征 12
2.4 实验设计 13
2.4.1温度对金属聚合物胶体及其性能的影响 13
2.4.2 稳定剂对金属聚合物胶体及其性能的影响 14
2.4.3 搅拌对金属聚合物胶体及其性能的影响 15
2.4.4超声波对金属聚合物胶体及其性能的影响 16
2.4.5 烧结温度对金属聚合物胶体及其性能的影响 17
2.5 实验仪器与药品 18
3 实验数据与分析 19
3.1 温度对金属聚合物胶体及其性能的影响 19
3.1.1 反应温度为0℃ 19 金属聚合物复合胶体制备研究+文献综述:http://www.751com.cn/huaxue/lunwen_3431.html