聚甲基丙烯酸聚异丙基丙烯酰胺互穿网络水凝胶的制备

摘要：基本材料是甲基丙烯酸/N-异丙基丙烯酰胺，交联剂是N,Nˊ-亚甲基双丙烯酰胺，引发剂是过硫酸钾。使用的方法是分步法，先制备甲基丙烯酸（MAA）与N,Nˊ-亚甲基双丙稀酰胺（MBA）共聚物水凝胶，再制备互穿网络水凝胶。从实验中可以看出，温度、pH、氯化钠溶液的浓度都会影响互穿网络水凝胶的溶胀率。42921

毕业论文关键词：聚甲基丙烯酸；聚异丙基丙烯酰胺；互穿网络水凝胶；温度敏感性；pH敏感性；溶胀率

Preparation of polymethyl methacrylate / Poly isopropylacrylamide interpenetrating network hydrogel

Abstract: The basic material is methyl acrylic acid/N-isopropylacrylamide and cross-linking agent is N,N '-methylene double acrylamide and initiator is potassium persulfate, interpenetrating network hydrogel were synthesized by a sequential IPN method. First investigated methylacrylic acid methacrylic acid (MAA) and N,Nˊ-methylene double propylene amide copolymer hydrogel (MBA), then preparation of interpenetrating network hydrogel. Can be seen from the experiment, the temperature, pH, the concentration of sodium chloride solution will affect the swelling rate of the interpenetrating network hydrogel.

Key Words: Poly methylacrylic acid; Poly isopropyl acrylamide; Interpenetrating network hydrogel; Temperature sensitivity; pH sensitivity; Swelling rate

摘要 1

引言 1

1 实验部分 2

1.1 实验试剂和仪器 2

1.2 甲基丙烯酸（MAA）与N,Nˊ-亚甲基双丙稀酰胺（MBA）共聚物水凝胶的制备 3

1.3 互穿网络水凝胶的制备 3

1.4 溶胀率SR的测定 3

1.5 互穿网络水凝胶的pH和温度敏感性 4

2 结果与讨论 4

2.1 互穿网络水凝胶在室温下和100 °C干燥箱内的失水率 4

2.2 互穿网络水凝胶溶胀动力学的测定 5

2.3 互穿网络水凝胶的温度敏感性的测定 6

2.4 互穿网络水凝胶pH敏感性的测定 7

2.5 互穿网络水凝胶在不同浓度盐溶液中溶胀率的测定 8

3 结论 9

参考文献 9

致谢 12

聚甲基丙烯酸/聚异丙基丙烯酰胺互穿网络水凝胶的制备

引言

水凝胶是非常特殊的分散体系，它是交联的高分子网络包裹水所组成的整体。在溶剂中，凝胶可以溶胀到一个平衡的体积仍然可以保持它的状态。水凝胶有很好的吸水性，能吸本身几十倍到几千倍的水，他也有很好的保水性，即使受到刺激也能保持水分不会流失。几年来，人们越来越关注能够受外界的环境的影响，从而本身的溶胀性能发生相应的变化的水凝胶的探索和研究。这些外部环境分别为：酸碱度和温度。当这些水凝胶受到外部环境的影响时，它们的溶胀率会随着外部世界的不同而发生不同的变化，这些特别的性质能够使这些水凝胶在医学，各种物质的分离等方面都有非常大的应用。.随着多肽药物、基因药物的出现，人们对这种同时具有多种响应性的水凝胶产生了极大的兴趣，并深入研究期望应用于日常的生产和生活中。聚甲基丙烯酸聚异丙基丙烯酰胺互穿网络水凝胶的制备:http://www.751com.cn/huaxue/lunwen_43559.html