摘要以TEOS和精油的疏水性液滴为软模板,通过四乙氧基硅烷（TEOS）在细乳液液滴界面上的溶胶-凝胶过程被成功制备了一系列含不同精油的介孔二氧化硅纳米胶囊。通过干燥含有精油的二氧化硅纳米胶囊和聚合物胶乳颗粒的混合乳液来实现精油/二氧化硅纳米胶囊对聚合物膜的芳香整理。精油/二氧化硅纳米胶囊均匀地分布在复合膜中。精油会缓慢但持续地释放出来，使复合膜保持长效的芳香效果。需指出的是，与精油/二氧化硅纳米胶囊复合后，聚合物膜的热和机械性能有所下降。44066
毕业论文关键词：细乳液;精油;二氧化硅纳米胶囊;复合膜;持续释放
Abstract
Mesoporous silica nanocapsules containing a series of fragrances were successfully prepared through an interfacial sol–gel process of tetraethoxysilane (TEOS) in miniemulsions. The hydrophobic liquid droplets of TEOS and fragrance worked as soft templates for forming a capsule morphology. The fragrance/silica nanocapsules were used to aromatically finish polymer films through drying a mixed emulsion of the fragrance/silica nanocapsules and polymer latex particles. The fragrance/silica nanocapsules were homogenously distributed in the composite films. The release of fragrances from the composite film displayed a slow and sustained manner. The introduction of the fragrance/silica nanocapsules could reduce the thermal and mechanical properties of the composite films.
Keywords: Miniemulsion; fragrance; silica nanocapsules; composite film; sustained release
目 录
1.引言 4
2实验部分 6
2.1原料 6
2.2 精油/SiO2纳米胶囊的制备 6
2.3 聚丙烯酸酯乳液的制备 7
2.4精油二氧化硅纳米胶囊/聚丙烯酸酯乳液复合膜的制备 7
2.5表征 8
3.结果与讨论 9
3.1含有不同精油的纳米胶囊的制备 9
3.2二氧化硅纳米胶囊/聚丙烯酸酯乳液的复合膜的制备 11
3.2.1复合膜的热学性质 13
3.2.2 机械性能 15
3.2.3 控制释放 16
3.3复合膜中精油的释放过程 18
4、结论 20
参考文献 21
致谢 24
1.引言
由于其独特的香和治疗功能，芳香剂被广泛用于化妆品、医药工业、农业和其它日用品中[1-4]。通常情况下，当精油暴露在空气中时，它容易挥发或氧化变质。因此，在布上直接涂上精油这种传统工艺不能起到长期的芳香整理效果。而将精油进行微胶囊化或纳米胶囊化则可以有效地克服上述问题[5]。
近年来，微米级和纳米级胶囊的制备已经引起了大众关注。多种多功能材料都已被用作胶囊壳的材料，如聚合物，无机和混合材料等[6-8]。 Podshivalov等人通过界面聚合法在油水乳液中合成了含有高良姜挥发油的聚氨酯 - 聚脲微胶囊[9]，并且发现，改变搅拌速度可以在在微米范围改变胶囊的颗粒大小。马丁等人通过复凝聚法制备了含有百里香油的聚乳酸微胶囊。这种微胶囊是使用不同的亲水 - 亲油平衡值非离子表面活性剂作为胶体稳定剂形成的[10]。他们后续又研究了不同表面活性剂对微胶囊的包覆效率、形态和粒度分布造成的影响。到目前为止，大多数报告只是集中在微米级别的精油胶囊制备上。然而，微胶囊由于具有大的颗粒尺寸是难以渗透到纤维层内的，这限制了微胶囊对具有微米尺度的纤维织物的整理。 精油纳米胶囊的制备及缓释性研究:http://www.751com.cn/huaxue/lunwen_45232.html