摘要本文主要研究了硼粉的表面包覆工艺。通过固液反应球磨法对硼粉进行表面包覆，包覆剂包括纳米镍粉、纳米铜粉、氧化铜、HTPB以及它们的混合物。采用XRD、SEM等仪器对包覆后的样品进行表征分析，最后运用远红外测温仪检测产物的燃烧性能。实验结果表明大多数产物的燃烧温度和燃烧速度都有所提高，其中HTPB和纳米镍粉包覆的硼粉燃烧温度提高到了1441℃，HTPB包覆的硼粉燃烧温度提高到了1236℃，纳米铜粉包覆的硼粉燃烧温度提高到了1219℃；燃烧速度提高最明显的是纳米镍粉包覆的硼粉，其质量燃烧速度提高了277%，线燃烧速度提高了191%。44994
关键词： 硼粉 燃烧性能 球磨法 包覆
毕业论文设计说明书外文摘要
Title The industrialized treatment technology of high combustion efficiency boron powder
Abstract
This paper studies the process of surface-coated boron powder. By reaction milling method of boron powder surface coating, coating agents including nano-nickel powder, nano-copper powder, copper oxide, HTPB, and mixtures thereof. By XRD, SEM and other equipment after the coated samples were characterized and analyzed, and finally the use of far-infrared thermometer to detect the combustion performance of the product. Experimental results show that the combustion temperature and combustion rate has increased in the majority of products, which HTPB and nano-nickel powder coated boron powder combustion temperature increased to 1441 ℃, HTPB-coated boron powder combustion temperature increased to 1236 ℃; combustion speed is the most obvious nano nickel powder coated boron powder, the mass burning rate increase 277% linear burn rate increase by 191%.
Keywords boron powder combustion ball milling surface-coating
目 次
1 绪论 1
1.1 硼粉在推进剂中的应用 1
1.1.1 复合推进剂的组分 1
1.1.2 硼粉的理化性质 3
1.1.3 硼粉在复合推进剂中的应用 4
1.2 硼粉表面改性的研究进展 5
1.2.1 硼粉表面的无机金属材料改性 5
1.2.2 硼粉表面的有机材料改性 5
1.3 本课题研究的主要内容 5
2 硼粉的表面包覆改性 6
2.1 超细粉体的表面包覆原理 6
2.2 超细硼粉表面包覆方法 6
2.3 实验试剂及仪器 6
2.3.1 实验试剂 6
2.3.2 实验仪器 6
2.4 硼/纳米镍复合粒子的制备 7
2.4.1 引言 7
2.4.2 实验过程 7
2.5 硼/纳米铜复合粒子的制备 8
2.5.1 引言 8
2.5.2 实验过程 8
2.6 硼/氧化铜复合粒子的制备 8
2.6.1 引言 8
2.6.2 实验过程 8
2.7 硼/HTPB复合粒子的制备 9
2.7.1 实验过程 9
2.8 硼/HTPB/纳米镍粉复合粒子的制备 10
2.8.1 实验过程 10
2.9 硼/HTPB/纳米铜粉复合粒子的制备 10
2.9.1 实验过程 10
2.10 硼/HTPB/氧化铜复合粒子的制备 11 高燃烧效率硼粉的可工业化处理技术研究:http://www.751com.cn/huaxue/lunwen_46253.html