摘 要：本论文以硝酸铈、1-苯基-3-甲基-4-苯甲酰基-5-吡唑啉酮（HPMBP）    2,6-吡啶二甲酸(DPCA)为原料，采用回流冷凝法，制备了一类新型稀土三元配合物，通过元素分析、紫外-可见光谱、XRD、热重-差热分析等手段对其进行了表征，推断该配合物的结构式可能为：Na2[Ce(HPMBP)3(DPCA)].3H2O,（HPMBP=1-苯基-3-甲基-4-苯甲酰基-5-吡唑啉酮，DPCA =2,6-吡啶二甲酸）。抗菌实验结果表明，稀土三元配合物对大肠杆菌具有一定的抑制作用，且抑菌效果优于单独配体。58324

毕业论文关键词：稀土，抗菌，配合物

Abstcrat:A new solid complex had been synthesized by the reaction of lanthanide with cerium nitrate, HPMBP and DPCA by condensation method. The composition of the complexes had been characterized by elemental analysis, FT-IR spectra, UV-Vis spectra and DTA-TGA analysis. The formula of complexes maybe is  Na2[Ce(HPMBP)3(DPCA)]·3H2O. The antibacterial activity testing shows that the complexes exhibit antibacterial ability against Escherichia coli. The antimicrobial spectrum of the complexes is better than single ligand.

Key words: Rare earth, Antibacterial, Complexes

1 前言 5

1.1抗菌的概念 5

1.2未来抗菌剂的应用发展趋势 5

1.3稀土配合物抗菌剂研究[6] 5

1.4回流冷凝法 5

2.1 试剂和药品 6

2.2测试仪器和方法 7

2.3试剂的配制 7

2.3.1  0.02mol/L标准Zn2+溶液的配制 7

2.3.2  0.02mol/L EDTA标准溶液的配制 7

2.3.3  0.5%二甲酚橙溶液的配制 7

2.3.4  20%六次甲基四胺溶液的配制 7

2.3.5  EDTA溶液的标定 7

2.4三元配合物的合成 8

2.5稀土（Ce）含量的分析 8

2.6板抑菌圈法 8

2.6.1抗菌实验 8

3、 结果与讨论 8

3.1配合物的组成与一般性质 8

3.2红外光谱分析(IR) 9

3.3紫外光谱分析(UV) 11

3.4 XRD谱图 11

3.5 TG-DTA谱图 12

3.6 配合物的抑菌实验 12

3.6.1抑菌结果分析 12

结  论 14

参考文献 15

致   谢 17

1 前言

微生物是导致传染病流行最重要的影响因素之一。在人类疾病中有50%是由病毒引起。药物和保健品是人类战胜疾病和提高生活质量的重要物质资源。人类在疾病的诊断和治疗过程中获得了显著的进步，但是随着人口急剧增长、环境逐步恶化，使得即使在科技发达的现代社会,人类仍然面临各种危险疾病的威胁，甚至某些疾病世界上至今无法治疗。同时，药物滥用情况日益严重，病原微生物的耐受和抵抗能力空前提高，使得原有效的药物效用大幅度降低，甚至药效尽失。所以我们为保护人类的身体健康必须开发更多有效的抗菌剂来。 回流冷凝法新型稀土三元配合物制备和表征:http://www.751com.cn/huaxue/lunwen_63226.html