3. The surface of the mold heat treatment to strengthen the quality and impact on life
Mold heat treatment the nature and quality of life of the mold a great impact. Practice shows that the die parts of the quenching distortion and cracking, early fracture during use, while the metallurgical and materials quality, forging quality, mold structure and process related, but related more to die of heat treatment. According to statistical analysis of failure causes of mold, heat treatment failure due to improper accounting for more than 50%. Practice shows that the mold material must be accompanied by high heat treatment process properly, can really play a material's potential. Parts surface hardening mold work purpose is to obtain the effect of external hard tough inside, so be hardness, wear resistance, toughness, good resistance to fatigue with. Many ways to die surface hardening, surface treatment technology of new technologies developed rapidly. In addition to Nitrocarburizing and ion nitride, boride, seepage niobium, vanadium permeability, hard chrome plated and spark strengthening, the chemical vapor deposition (CVD) and physical vapor deposition (PVD) has been gradually adopted. By CVD and PVD treatment, the mold surface covered with super-hard material, such as TiC, TiN, etc.. High hardness, wear resistance, corrosion resistance, adhesion is very good, can improve the die life several times to several times.
4. Manufacturing precision of the die parts of die life
Precision die manufacturing and life in it in particular, mold surface roughness on the mold a great impact. If using Crl2MoV steel blanking die, if the surface roughness value R = 1.6 m, its life span is about 30,000. Such as polished by the precision, surface roughness value R = 0.4 m, life can be increased to 4-5 million. Therefore, the working parts of the mold surface, the general must go through grinding, grinding, polishing and other finishing and fine processing.
5. Other aspects of the impact of die life
(1) Press the accuracy is not high, but also easy to make die damage.
(2) die in the press or not installed properly and the operator's technical level, on the tool life is also greatly affected.
(3) dies in the custody and maintenance of good and bad, and the use of lubricant condition also affects mold life.
6. Conclusion
In actual production, sheet metal dies for use, rare case of non-normal wear and tear. But when the die plate was found prone to irregular wear, we always study for the problems summarized. Because of a cold die, from the design, manufacture, assembly, commissioning and installation and use, all spent many hours, while the convex die, die material used, mostly high-quality alloy steel. Therefore, the die cost is relatively high. Therefore, in the production of understanding the factors that affect the die life and take the appropriate measures to guide the production of great practical significance.
冷冲模具使用寿命的影响及对策
冲压模具概述
冲压模具--在冷冲压加工中，将材料（金属或非金属）加工成零件（或半成品）的一种特殊工艺装备，称为冷冲压模具（俗称冷冲模）。冲压--是在室温下，利用安装在压力机上的模具对材料施加压力，使其产生分离或塑性变形，从而获得所需零件的一种压力加工方法。
冲压模具的形式很多，一般可按以下几个主要特征分类：
１．根据工艺性质分类 论文网
　　（1）冲裁模 沿封闭或敞开的轮廓线使材料产生分离的模具。如落料模、冲孔模、切断模、切口模、切边模、剖切模等。
（2）弯曲模 使板料毛坯或其他坯料沿着直线（弯曲线）产生弯曲变形，从而获得一定角度和形状的工件的模具。
（3）拉深模 是把板料毛坯制成开口空心件，或使空心件进一步改变形状和尺寸的模具。
　　（4）成形模 是将毛坯或半成品工件按图凸、凹模的形状直接复制成形，而材料本身仅产生局部塑性变形的模具。如胀形模、缩口模、扩口模、起伏成形模、翻边模、整形模等。 冷冲模具使用寿命英文文献和中文翻译(5):http://www.751com.cn/fanyi/lunwen_30866.html