核/壳结构硅橡胶粒子制备及其改性聚乳酸研究

摘要制备了具有核/壳结构的纳米级硅橡胶粒子(NSRP)，并对粒子进行一系列性能测试。用NSPR对聚乳酸(PLA)进行改性，包括两部分：仅用NSRP改性PLA，用NRSP和磷系阻燃剂(PX-220)复配改性PLA。结果表明，仅用NSRP改性的PLA阻燃性及热稳定性提高不明显；在粒子添加量在3-6%时强度下降最小，韧性提高最大，结晶性改善明显。NSRP与PX-220复配使用时，少量NSRP即可改善PLA燃烧熔滴现象，加入量大会导致阻燃性下降，在实验配方中，PLA/PX-220/NSRP为75/22/3时效果最好。19111
关键词核壳结构硅橡胶粒子聚乳酸结晶阻燃
毕业论文设计说明书(论文)外文摘要
Title Study and preparation of PLA modified by NSRP
Abstract
Nano silicon rubber particles (NSRP) were prepared by seed emulsion polymerization. A series of test of the particles were carried out. PLA was respectively modified by NSRP alone and by the blends of core/shell NSRP and phosphorus flame retardant (PX-220). The results show that when core/shell NSRP were used alone, the modified PLA shows no significantly improved flammability or thermal stability in all formulas but remarkable increased toughness and crystallinity and little loss of tensile strength when particle proportion is between 3% and 6%. When NSRP were used together with PX-220, a little addition of NSRP improves the phenomenon of droplet while high content of NSRP makes the flammability of the modified PLA bad. In all tested formulas, proportion 75/22/3(PLA/PX-220/NSRP) gives the best comprehensive effect.
(空2行)
Keywords core/shell silicon rubber particle PLA crystallinity
flammability
目   录
1 绪论    1
1.1 研究背景    1
1.1.1 PLA材料的发展历程    1
1.1.2 PLA材料的性质及应用    1
1.1.3 PLA的主要改性方法    2
1.2 研究现状    2
1.2.1 PLA纳米复合材料的研究现状    2
1.2.2 核壳结构NSRP的特点    2
1.3 研究意义及内容    2
2 核壳结构硅橡胶粒子的制备、结构表征及热性能研究    4
2.1 概述    4
2.2 实验部分    4
2.2.1 实验原料与仪器    4
2.2.2 MMA的精制    5
2.2.3 核壳结构硅橡胶粒子的制备    5
2.2.4 性能测试    6
2.3 结果与讨论    7
2.3.1 核壳粒子结构的设计    7
2.3.2 核壳粒子的表征和结构分析    7
2.3.3 核壳结构硅橡胶粒子的热稳定性能分析    10
2.4 本章小结    10
3 核壳粒子改性PLA的制备、力学性能、结晶性能及热性能研究    12
3.1 概述    12
3.2 实验部分    12
3.2.1 实验原料与仪器    12
3.2.2 核壳结构硅橡胶粒子改性PLA的制备    13
3.2.3 性能测试    13
3.3 结果与讨论    14
3.3.1 核壳粒子改性PLA的力学性能    14
3.3.2 水的静态接触角测试    15
3.3.3 改性PLA中核壳粒子分散性观察    16 核/壳结构硅橡胶粒子制备及其改性聚乳酸研究:http://www.751com.cn/huaxue/lunwen_10327.html