摘要本文在碱性化学镀镍的基础上来,研究了有机防变色处理液的组成及工艺条件改变对化学镀镀镍层的防变色处理效果。改变温度、氧化剂含量以及浸泡时间等因素来对化学镀镍片进行防变色处理。通过交流阻抗及线性极化曲线等测试来评价防变色处理效果。研究结果显示：镀镍片的防变色性能随防变色处理浸泡时间增大而增加；有机氧化剂用量的增加有利于提高防变色的处理效果。防变色处理效果随温度的变化，镀镍片性能随着有机氧化剂量增加而变好以及其性能和温度无线性关系。20145
关键词： 镀镍 防变色 交流阻抗 线性极化
Abstract
Based on the basic chemical nickel plating, this dissertation have the purpose to study organic antitarnish treatment liquid composition and certain of conditions change effect of anti chemical plating nickel layer. Changing condition in temperature, oxidant concentration and soaking time and other factors can contribute to wheather the chemical nickel plating film antitarnish treatment performance changed. The AC impedance and linear polarization curve test can evaluate anti tarnishing treatment effect. Research results show that: the nickel sheet properties performance have positive linear correlation with the increase of  immersion time and the  increase of organic oxidation dose while its temperature increase change can not find linear correlation. .
Key words: linear polarization plate-nickle anti-tarnishing AC impedance
目录
1 绪论    1
1.1.1 化学镀镍机理    1
1.1.2 化学镀镍的优点    2
1.1.3 化学镀镍的发展    2
1.1.4  化学镀镍液的类型    3
1.2化学镀镍的腐蚀变色    4
1.2.1腐蚀的概念    4
1.2.2 腐蚀的形态    5
1.2.3 腐蚀的因素    5
1.2.4 镍的腐蚀变色原理    5
2 文献综述    6
2.1 镍磷合金层防变色    6
2.2 黑镍防变色    6
2.3 镍铬防变色    7
3 本论文选题的目的、方案论证及研究的主要内容    8
4 实验部分    9
4.1 实验的仪器和试剂    9
4.1.1 实验仪器    9
4.1.2 实验试剂    9
4.2 实验步骤    10
4.2.1 预处理    10
4.2.2 实验过程    11
4.2.3实验分析    11
5 结果与讨论    13
5.1 结果    13
5.2 结论    20
致谢    21
参考文献    22
 
镀镍层防变色处理液的性能评价
1 绪论
　　一般镀镍层是多孔的，所以除某些医疗器械外，镍常常与其他金属镀层组成多体系来降低镀层的抗腐蚀性能，有时也做为碱性介质的保护层。
化学镀的积极方面是不可代替的.具体说来,化学镀层的物理化学特性吸引了许多学者和科研人员的研究,尤其是在它的均匀性能以及抗磨性能还有抗腐蚀性能上。化学镀镍层的应用非常广泛，对于工业需求，该项技术已经影响着整个电镀行业甚至更多。化学镀在各个工业的应用也有着举足轻重的地位，更值得一提的是，一个行业的重要性与其的未来发展是有着密切联系的，因此当化学镀镍经以20%到30%年平均增加速率的历了20世纪末的高速发展后。在现在这个21世纪，其发展以7%左右逐渐走向成熟期。但是值得注意的是，在经济横飞的东南地区，尤其是中国，化学镀可以作为一种新兴产业值得所有人青睐由于它的蓬勃发展。 镀镍层防变色处理液的性能评价:http://www.751com.cn/huaxue/lunwen_11805.html