摘要：本课题主要研究了一种强酸性阳离子交换树脂及其环保型制备方法。该树脂通过运用相转移催化原理将水溶性的不饱和烷基（芳基）磺酸盐与质子化的三辛胺反应制备出油溶性的不饱和烷基（芳基）磺酸-三辛铵单体，然后以这种不饱和烷基（芳基）磺酸-三辛铵单体、苯乙烯为单体为原料，以二乙烯基单体为交联剂，通过自由基引发的悬浮聚合制备出的强酸性阳离子交换树脂。本课题制备的强酸性阳离子交换树脂为粒径范围0.5～1.2mm的白色球形颗粒，其磺酸基团的含量为23.5～29.2%，离子交换容量为2.91～3.64meq/g。20654
毕业论文关键词： 离子交换树脂；乙烯基磺酸盐；相转移催化；硫含量；离子交换容量
Research on the preparation of cation exchange resin by vinyl sulfonate
Abstract: The main subject of study of a strong acid cation exchange resin and environmentally friendly production method. The resin obtained by using the principle of phase transfer catalysis to the water-soluble unsaturated alkyl (aryl) into an oil-soluble sulfonate, and styrene as monomer, crosslinker pinyl monomer by radical suspension-induced polymerization of the strong acid cation exchange resin. Strongly acidic cation exchange resin prepared in the subject range white spherical particles with a particle diameter of 0.5 ~ 1.2mm, and the sulfonic acid group content of 23.5 ~ 29.2%, an ion exchange capacity of 2.91 ~ 3.64meq / g.
Key Words：Cation exchange resin；vinyl-sulfonate；Phase transfer catalysis；Sulfur content；Ion exchange capacity
目录
1 绪论 1
1.1阳离子交换树脂的概述 1
1.2阳离子交换过程 2
1.3阳离子交换树脂的发展趋势 3
1.4强酸型阳离子交换树脂的概述 4
1.5传统强酸性阳离子交换树脂制备存在的问题 4
1.6乙烯基磺酸盐概述 5
1.7相转移催化的概述 6
1.8研究意义及目的 9
2 实验 10
2.1 试剂及仪器 10
2.2 乙烯基磺酸盐——苯乙烯聚合原理 10
2.2.1 悬浮聚合机理 10
2.2.2 相转移催化的原理 11
2.2.3 离子交换树脂的共聚球形颗粒水解原理 12
2.3 乙烯基磺酸盐——苯乙烯共聚物合成制备工艺 13
2.4 乙烯基磺酸盐——苯乙烯共聚物的性能测定 15
2.4.1 粒径测定 15
2.4.2 含水量测定 16
2.4.3阳离子交换树脂交换容量测定 16
2.4.4 硫含量测定 17
2.4.5 红外测定 18
3结果与讨论 19
3.1 阳离子交换树脂制备工艺 19
3.2 油溶性TOA-MS88制备条件 19
3.3悬浮聚合工艺条件 20
3.3.1 分散剂的影响 20
3.3.2 引发剂的影响 21
3.3.3 反应温度及升温速度的影响 21
3.3.4 搅拌速率的影响 22
3.4 交换树脂预聚体水解条件 23
3.5 乙烯基磺酸盐——苯乙烯共聚物的表征及性能分析 25
3.5.1粒径分布分析 25
3.5.2红外表征分析 26
3.5.3磺酸盐含量分析 27
4研究结论 29
致谢 30
参考文献 31
附录1：设备 33
1 绪论
1.1阳离子交换树脂的概述
离子交换树脂是一类带有功能基的网状结构的高分子化合物，其结构由三部分组成：不溶性的三文空间网状骨架，连接在骨架上的功能基团和功能基团所带的相反电荷的可交换离子。根据树脂所带的可交换的离子性质，离子交换树脂可大体上分为阳离子交换树脂和阴离子交换树脂。 基于乙烯基磺酸盐制备阳离子交换树脂的研究:http://www.751com.cn/huaxue/lunwen_12513.html