锌镀层蓝白色钝化溶液的研究

摘要：由于751价铬的高毒性,镀锌层三价铬钝化工艺是一种替代751价铬钝化工艺的良好选择。其中三价铬蓝白钝化是一种优良的防护装饰性膜层。详细阐述了影响蓝白色钝化膜性能的主要因素。经过不断的试验,研究出了一种组分简洁的镀锌层三价铬蓝白色钝化液,性能稳定,外观和耐蚀性优良。22473
毕业论文关键词：三价铬蓝白色钝化工艺；钝化膜；耐蚀性；锌镀层
Study on zinc plating bright blue passivation solution
Abstract: Hexavalent chromium is a high toxicity material and may cause environment pollution .And trivalent chromium passivation film is an excellent protective and decorative film on zinc coating .A new kind of trivalent chromium bright blue passivation process with simple components and stable bath and with excellent performance of film was developed. The influence factors for the performance of trivalent chromium bright blue passivation film are introduced.
Keywords: Trivalent Chromium Bright Blue Passivation； Passivation Film； Corrosion Resistance；Zinc Coating

目录
1. 前言    1
1.1 镀锌工艺的种类    1
1.1.1 碱性镀锌    1
    1.1.2 酸性镀锌    1
1.2 氯化钾镀锌工艺的发展    2
    1.2.1 第一代氯化钾镀锌    2
    1.2.2 第二代氯化钾镀锌    3
    1.2.3 第三代氯化钾镀锌    4
1.3 氯化钾镀锌工艺的条件控制    5
    1.3.1 镀液的成分和操作条件    5
    1.3.2 各种组分的作用及控制    5
1.4 三价铬蓝白色钝化工艺    7
    1.4.1 三价铬蓝白色钝化膜成膜机理    7
    1.4.2 三价铬蓝白色钝化剂的组成    8
    1.4.3 一般三价铬钝化溶液的配方和操作条件    9
    1.4.4 工艺流程    9
    1.4.5 钝化工艺条件的影响及控制    9
1.5 钝化膜耐腐蚀性的检测    10
    1.5.1 耐腐蚀性能测试的传统方法    10
    1.5.2 耐腐蚀性能测试的新方法    11
1.6 本课题的研究内容、目的及意义    12
2. 实验部分    13
2.1 化学试剂与仪器设备    13
    2.1.1 化学试剂    13
    2.1.2 仪器设备    13
2.2 实验过程    13
    2.2.1 各阶段溶液的组成和操作条件    13
    2.2.2 工艺流程    14
    2.2.3 实验过程    14
3. 结果及讨论    16
3.1 实验结果    16
3.2 结果分析    18
    3.2.1 钝化结果分析    18
    3.2.2 耐腐蚀性检测结果分析    18
3.3 钝化时间对钝化膜的影响    19
3.4 钝化温度对钝化膜的影响    19
3.5 钝化时间和温度对钝化膜耐腐蚀性的影响    20
4. 结论    21
致谢    22
参考文献    23
1.前言
1.1 镀锌工艺的种类
1.1.1碱性镀锌
镀液呈强碱性。因络合剂不同又分为氰化物镀锌和锌酸盐镀锌两种。
（1）氰化物镀锌溶液中使用氰化钠做络合剂，氢氧化钠做辅助络合剂兼导电盐。氧化锌或氰化锌做主盐。这种镀液稳定，具有良好的均镀能力。镀层细致，耐蚀性好，镀层脆性小，易二次加工。加入光亮剂后壳获得酷似亮铬般的镀层。电流效率较低。锌镀层蓝白色钝化溶液的研究:http://www.751com.cn/huaxue/lunwen_15126.html