摘要：为了研究稀土对铜化学防变色的影响，我们最开始寻找了BTA缓蚀剂对铜防变色的影响以及BTA的最佳使用条件，得出BTA的最佳使用浓度是5.2g/L，使用温度是40℃，处理时间是30min。在这个条件下，我们将BTA分别与硝酸镧和硝酸铈分别进行复配，发现硝酸铈对铜化学防变色效果更好，用量更少，仅仅为0.2g/L。38635
毕业论文关键词：BTA，线性极化，交流阻抗，硝酸铈，硝酸镧
Rare earth elements on copper surface and the effect of the chemical prevent discoloration
Abstract: In order to study the effect of rare earth chemical prevent discoloration of copper, we started looking for the BTA corrosion inhibitors on copper prevent discoloration and the effect of BTA in the best conditions of use, obtained the best use of the BTA concentration is 5.2 g/L, using temperature 40 ℃, the processing time is 30 min. In this condition, we used BTA to combination with lanthanum nitrate and cerium nitrate respectively, found that cerium nitrate is better for its effects of copper chemical, dosage is less, only 0.2 g/L.
KeyWords：BTA，linear polarization，EIS，lanthanum nitrate，cerium nitrate
目录
1.绪论    1
1.1铜的基本介绍和性质描述    1
1.2造成铜腐蚀变色的因素    1
1.3铜防腐蚀方法    2
1.3.1涂清漆    2
1.3.2自组装膜对铜的防腐蚀    2
1.3.3利用缓蚀剂对铜进行防护    3
1.4铜保护膜的类型    3
1.5我国在防止铜变色方面的研究现状    4
1.6一般缓蚀剂应用列举    4
1.6.1苯并三氮唑在防止铜变色应用    4
1.6.2ATA缓蚀剂在防止铜变色方面的的研究    5
1.6.3巯基苯并恶唑对铜缓蚀作用研究    5
1.6.4新型缓蚀剂Bis-triazole对铜的缓蚀效果研究    6
1.7稀土金属作为缓蚀剂的应用    6
1.8稀土金属缓蚀剂的协同作用研究    7
1.9本论文的工作    7
2.实验部分    9
2.1试剂    9
2.2仪器    9
2.3试验方法    9
2.3.1失重法    9
2.3.3硝酸腐蚀法    10
2.3.4电化学方法    10
2.4前处理过程    12
2.4.1除油液工艺配方    12
2.4.2酸洗工艺配方    13
2.4.3抛光液工艺配方    13
2.5测量过程    13
3.实验结果与分析    15
3.1 不同浓度的BTA对铜的缓蚀效果    15
3.1.1不同浓度的BTA对铜的缓蚀效果的线性极化分析    15
3.1.2不同浓度的BTA对铜的缓蚀效果的交流阻抗分析    16
3.1.3硝酸滴片实验    17
3.1.4盐水浸泡实验结果分析    18
3.2不同温度的BTA对铜的缓蚀效果研究    19
3.2.1不同浓度的BTA对铜的缓蚀效果的线性极化分析    19
3.2.2不同浓度的BTA对铜的缓蚀效果的交流阻抗分析    20
3.2.3 不同温度处理的铜片的硝酸滴片    21
3.2.4 不同温度处理的铜片的盐水浸泡实验    22
3.3 BTA缓蚀剂处理不同时间影响    23
3.3.1 BTA缓蚀剂处理不同时间后的铜片在3%氯化钠中的线性极化    23
3.3.2  BTA缓蚀剂处理不同时间后的铜片在3%氯化钠中的电化学阻抗    24
3.3.3  经BTA不同处理时间的铜片的硝酸滴片    25 稀土对铜表面的化学防变色的影响:http://www.751com.cn/huaxue/lunwen_37656.html