摘 要: 利用4-硝基苯异氰酸酯对凹凸棒土进行有机改性，通过红外（IR）、X-射线衍射仪（XRD）、比表面积测定（BET）、热重分析等分析方法对改性前后凹凸棒土进行了表征。结果表明，改性后的凹凸棒土的表面积比改性前的凹凸棒土表面积小，用改性后的凹凸棒土对亚甲基蓝进行吸附试验。结果表明，改性凹凸棒土使亚甲基蓝试剂的脱色率明显提高。64087

毕业论文关键词: 凹凸棒土, 4-硝基苯异氰酸酯, 有机改性, 亚甲基蓝, 吸附

Abstract: The attapulgite powders were organically modified using 4-nitrophenyl isocyanate , The pristine and modified attapulgite powders were characterized by IR, XRD, TG, BET. The results showed that the main interaction between attapulgite surface and 4-Nitrophenyl isocyanate are chemical bonds. Although the specific surface area of modified attapulgite decreased comparing pristine attapulgite powders, the decolorization rate for methylene blue increased to 99%. 

Keywords: Attapulgite powder, 4-nitrophenyl isocyanate, Rganically modified, Methylene blue, Adsorption

1 前言 4

2 实验部分 4

2.1 实验原料 4

2.2 实验方法 4

3 结果与讨论 5

3.1 改性凹凸棒土表征 5

3.1.1凹凸棒土改性前后红外光谱分析 5

3.1.2 凹凸棒土改性前后XRD分析 5

3.1.3 凹凸棒土改性前后比表面分析 7

3.1.4 凹凸棒土改性前后热重分析 8

3.2 分光光度法研究凹凸棒土对亚甲基蓝的吸附 10

3.2.1 亚甲基蓝最大吸收波长的确定 12

3.2.2 吸附用量的确定 11

3.2.3 吸附平衡时间的确定 12

3.2.4 温度对吸附平衡的影响 13

3.2.5 等温吸附曲线的确定 14

结论 15

参考文献 16

致谢 17

 1 前言

   凹凸棒土是一种晶质水合镁铝硅酸盐矿物[1]，它的链层状晶体结构很独特，所以拥有许多特殊的物化性能。主要包括吸附性、催化性和可塑性等[2-4]。由于凹凸棒土的这些特性，被广泛的应用于化工、建材、医药、环保、生活用品等诸多领域[5-7]。

   凹凸棒土的表面带负电荷以及含有大量的极性硅羟基，导致凹凸棒土表面覆盖有一层水膜，这极大限制了凹凸棒土在某些领域的应用[8]。因此，在实际应用中，使用前通常对凹凸棒土进行改性处理，以改善凹凸棒土的使用效果，达到不同的目的。论文网

   本文采用4-硝基苯异氰酸酯对凹凸棒土进行改性，为其在有机废水治理中的应用提供依据[9]。

2 实验部分

2.1 实验原料

   凹凸棒粘土（江苏盱眙）；盐酸；甲苯；蒸馏水；氨基丙基三甲氧基硅烷；4-硝基苯异氰酸酯；亚甲基蓝。除凹凸外所用试剂均为分析纯。

2.2 实验方法

   2.2.1 凹凸棒土预处理：取一定量的凹凸棒土加入浓度4mol/L的稀盐酸溶液，用搅拌机以200 r / min 速度搅拌24小时，自然静置，过滤，用蒸馏水洗涤至溶液呈中性(不含氯离子)，然后过滤，于烘箱105℃下干燥，得到凹凸棒土1。 4-硝基苯异氰酸酯改性凹凸棒土吸附亚甲蓝研究:http://www.751com.cn/huaxue/lunwen_71010.html