摘  要：本论文以改性介孔硅基材料SBA-15（SA-SBA-15）作为课题研究对象，通过使用N2吸附/脱附等温线（BET）、X射线衍射(XRD)、透射电子显微镜(TEM)、差热-热重（DTA-TG）、傅立叶红外(FT-IR)等对改性介孔硅基材料SBA-15进行了表征。分析结果表明改性介孔硅基材料SBA-15的表面可以很好的包裹席夫碱。然后对改性介孔硅基材料SBA-15进行水体中Cu2+的吸附实验，发现其对铜离子的吸附能力较强，吸附剂用量达到50 mg时，实验条件下，吸附容量达到饱和；Cu2+的吸附随pH呈波动性变化，pH为5时处理效果最好；经过硝酸处理的SA-SBA-15在经历三个再生周期后仍然保持良好的吸附能力。68681

毕业论文关 键 词：SBA-15，废水，铜离子，吸附

Abstract: Popular materials Mesoporous Silica materials SBA-15 were as the research object in this paper. Mesoporous Silica materials SBA-15 were characterized by the images of DTA-TG, X-ray diffraction patterns (XRD), transmission electron microscope (TEM), Fourier transform in-frared (FT-IR), adsorption and stripping isotherm of nitrogen. This experimental process indicates that Mesoporous Silica materials SBA-15 can very good pack the Schiff base. Then we research the absorption ability of the metals, we discover that they have a very good absorption toward inorganic metal copper ion. When the adsorbents are about 50 mg, the adsorption capacity is in the highest point. The adsorption of copper ion will change with the pH. There will have a effective treatment effect at 5. The SA-SBA-15 treated with nitric acid still keeps good adsorption capacity after three regeneration cycle.

Keywords: SBA-15, Waste Water, Copper, Absorption 

目  录

1  前言 5

1.1  分子筛的定义 5

1.2  分子筛的分类 5

1.3  分子筛的特点 5

1.4  SBA-15的研究发展 5

1.5  SBA-15的化学改性 6

2  实验部分 7

2.1  实验仪器 7

2.2  试剂和药品 7

2.3  材料的合成 7

2.3.1 SBA-15的合成 7

2.3.2共缩聚法合成氨基改性SBA-15 8

2.3.3后嫁接法合成氨基改性SBA-15 8

2.3.4席夫碱在SBA-15上的组装 9

2.4  材料的吸附性能研究 9

2.4.1吸附溶液的配制 9

2.4.2不同剂量吸附剂的影响 9

2.4.3 pH的影响 9

2.4.4吸附剂的再生 9

2.4.5吸附时间的影响 10

2.5  表征手段 10

2.5.1 X射线衍射-XRD 10

2.5.2透射电子显微镜-TEM 10

2.5.3元素分析-EA 10

2.5.4差热及热失重分析-DTA-TG 10

3  结果与讨论 10

3.1  表征分析 10

3.1.1 X射线衍射分析 11

3.1.2透射电子显微镜分析 改性介孔硅基材料SBA-15（SA-SBA-15）废水铜离子吸附:http://www.751com.cn/huaxue/lunwen_77288.html