摘要：氧化铈钴固溶体因拥有良好的储氧性能和较高的热稳定性以及优异的低温催化性能，被用作作汽车尾气净化催化剂载体，并受到广泛关注。本课题主要通过用蒸发诱导自组装的方法（EISA）来合成介孔铈钴固溶体。用非离子表面活性剂F127作为模板剂，正硅酸四乙酯和酚醛树脂分别作为无机和有机的前驱体，酚醛树脂，751水硝酸钴和751水硝酸铈分别作为碳，钴和铈的来源物质。用最佳的介孔氧化钴的比例作为基础模板再添加751水硝酸铈，通过改变这五种物质的摩尔量和控制反应条件来控制介孔的形成和比表面积、孔容的大小，用XRD，能谱图和N2吸脱附图来表征。10790
关键词：铈钴固溶体；介孔材料；EISA；氧化钴，氧化铈
The Controllable generation of Mesoporous Ce1-xCoxO2 Solid Solutions
Abstract：Mesoporous Ce1-xCoxO2 Solid Solutions have been synthesized via a facile evaporation induced triconstituent co-assembly (EISA) approach by using Pluronic F127 as a template and resol , Cobalt nitrate hexahydrate and Cerium nitrate hexahydrateare as carbon , Co and Ce sources. Moreover, soluble resol polymer is used as an organic precursor and prehydrolyzed TEOS is used as an inorganic precursor. The genetation of Cerium Cobalt Composite Oxide through filling Cerium nitrate hexahydrateare into Mesoporous Co3O4 is a effective way to conrol particle size , BET surface areas and pore volume. The samples were characterized by XRD，Energy spectrum diagram and nitrogen adsorption —desorption isotherms.
Keywords: Cerium cobalt oxide Composite Oxide; Mesoporous Material ; EISA ; mesoporous cobalt oxide，Cerium oxide
目录
1绪论 1
1.1 研究背景及意义 1
1.2 介孔氧化钴的合成及其意义 2
1.2.1介孔氧化钴的合成 2
1.2.2介孔氧化钴合成的意义 3
1.3 介孔氧化铈的合成及其意义 3
1.3.1介孔氧化钴的合成 3
1.4介孔氧化铈钴固溶体的合成 4
1.5介孔材料的表征 5
1.6 本课题的研究内容 6
2 实验部分 6
2.1 仪器与试剂 6
2.1.1 实验试剂 6
2.1.2 实验仪器 6
2.2 介孔氧化钴的制备 7
2.2.1实验步骤 7
2.2.2 介孔氧化钴的表征方法 8
2.2.3 制备介孔氧化钴的实例一 8
2.2.4 制备介孔氧化钴的实例二 9
2.2.5 制备介孔氧化钴的实例三 11
2.3 介孔氧化铈的制备 18
2.3.1实验步骤 18
2.3.2 制备介孔氧化铈的实例四 18
2.3.3 制备介孔氧化铈的实例五 20
2.4 介孔铈钴固溶体的制备 23
2.4.1实验步骤 23
2.4.2 制备介孔铈钴固溶体的实例一 23
2.4.3 制备介孔铈钴固溶体的实例二 26
2.4.4 制备介孔铈钴固溶体的实例三 28
2.4.5 制备介孔铈钴固溶体的实例四 33
2.4.6 制备介孔铈钴固溶体的实例四 36
3 结果与讨论 39
3.1 最佳介孔氧化钴的结果分析 39
3.1.1 XRD分析 39
3.1.2 扫描电镜SEM图的形貌分析 40
3.1.3 能谱图分析 41
3.2 最佳介孔氧化铈的结果分析 42
3.3 介孔铈固溶体的结果分析 42 介孔氧化铈氧化钴纳米孔材料的可控制备及性能研究:http://www.751com.cn/huaxue/lunwen_9928.html