摘要以废纸为基底原料，在加入耐火纤维与无机胶粘剂的基础上加入硅溶胶，制得纸质耐火材料。本文对含不同无机耐火纤维含量以及无机胶粘剂和硅溶胶不同配比的纸质耐火材料分别进行了三点弯曲强度测试、热失重测试以及900℃残炭量测试。测试表明，耐火纤维的含量会对样品的强度和耐高温性能产生一定影响。硅溶胶不仅可以减少样品的分层率也在一定程度上增加了样品的耐火性能。47655
Abstract: Waste paper as raw material base, adding silica sol adding refractory fiber and inorganic adhesive, based on a paper prepared refractories. In this article, different inorganic refractory fiber content as well as inorganic sol adhesives and refractories containing different proportions of the paper were carried out three-point bending strength test, test, and 900 ℃ TGA char residue. Tests showed that the strength and heat resistance of refractory fiber content of the sample would have an impact. Silica sol can not only reduce the sample rate also increases the layered fire resistance of the sample to a certain extent.
毕业论文关键词：无机耐火纤维;无机胶粘剂;硅溶胶;纸质耐火材料;制备;表征
Keyword：Inorganic refractory fiber; Inorganic adhesive; silica solution ;paper Refractories Preparation; Characterization
目 录
1.前言 4
2.实验部分 7
2.1.原料 7
2.2.主要实验仪器 7
2.3.纸质耐火材料试样制备 8
2.3.1.原料准备 8
2.3.2.纸质耐火材料样品的制备 8
2.4.性能测试与结构表征 8
2.4.1.三点弯曲测试 8
2.4.2.热失重测试分析 9
2.4.3.残炭量测试分析 9
3.结果与分析 10
3.1.三点弯曲测试分析 10
3.1.1.耐火纤维含量对弯曲强度和弹性模量的影响 10
3.1.2.硅溶胶与胶黏剂的不同配比时对弹性模量和弯曲强度的影响 12
3.2.热失重分析 13
3.2.1.耐火纤维对热失重的影响 13
3.2.2.硅溶胶与胶黏剂的配比对热失重的影响 14
3.3残炭量分析 15
3.3.1.耐火纤维对残炭量的影响 15
3.3.2.硅溶胶与胶黏剂的配比对残炭量的影响 16
4.总结 18
1.前言
铸造行业是制造业的主要组成部分，对我国经济发展有着非常重要的作用。我国铸造技术有悠久的历史，追溯到5000多年前，铸造技术就已经出现在中华大地上，铸造技术应用在农业生产、兵器制造甚至音乐艺术以及人民生活的各个方面，极大的推动了我国古代文明社会的发展。而浇道管在铸造过程中是不可缺少的一部分，其质量的优劣也决定了铸件的质量。
目前市场上用得较多的为陶瓷浇道管，纸质浇道管是陶瓷浇道管的替代产品，该产品已于2010年10月被宁夏铸造行业技术专家曹敏道等同志注册为国家专利[1]。纸质浇道管相对于陶瓷浇道管来说实现了废弃物的加工利用，不仅在使用过程中不会对铸件造成影响，而且在整个生产过程中不会产生任何的污染，更加的绿色环保。