摘要：本文主要研究MQ树脂的合成工艺流程，从甲基MQ树脂入手探索合成工艺，到最后成功合成苯基MQ树脂。比较水玻璃法和正硅酸乙酯法各自制备MQ 硅树脂的优劣。为了获取更高的收率，最终选用正硅酸乙酯法制备。讨论了在MQ硅树脂制备过程中的一些影响因素，比如投料比等对产物形态的影响。最后对获取的甲基MQ硅树脂和苯基MQ硅树脂做红外分析，结果表明：成功制备了苯基MQ硅树脂。22078
毕业论文关键词：有机硅树脂；性能；稳定性；MQ硅树脂；苯基MQ硅树脂
Preparation and Characterization of Phenyl MQ Resin
Abstract: This paper studies the synthesis process MQ resin, methyl MQ resin from start to explore the synthesis process, the last successful synthesis of phenyl MQ resin. Comparison of sodium silicate and TEOS method for preparing the pros and cons of each method MQ silicone resin. In order to obtain a higher yield, the final selection of equipment TEOS method. Discusses some of the factors in the process to prepare a silicone MQ resin, for example on the feed ratio of the product morphology. Finally MQ silicone resin obtained methyl and phenyl MQ silicone resin made infrared analysis.
Keywords: Silicone resin; performance; stability; MQ silicone resin; phenyl MQ silicone resin
目录
1绪论    6
1.1 有机硅树脂的概述    6
1.2 MQ硅树脂的概述    8
1.3 MDQ/MTQ树脂的概述    9
1.4苯基MQ树脂的概述    9
1.5研究意义及目的    10
1.6主要研究内容    11
2试验    12
2.1原料名称、规格和来源    12
2.2 MQ树脂合成机理以及基本反应    13
2.2.1硅酸钠法(水玻璃)    13
2.2.2正硅酸乙酯法    15
2.3甲基MQ树脂合成过程(硅酸钠法)    16
2.4.1合成原料    17
2.4.2甲基MQ树脂合成实验流程图    17
2.4.3甲基MQ树脂合成实验步骤    17
2.4甲基MQ树脂合成过程(硅酸脂法)    18
2.4.1合成原料    18
2.4.2甲基MQ树脂合成实验流程图    18
2.4.3甲基MQ树脂合成实验步骤    19
2.5苯基MQ树脂合成过程(硅酸脂法)    19
2.4.1合成原料    19
2.4.2苯基MQ树脂合成实验流程图    19
2.4.3苯基MQ树脂合成实验步骤    20
3结果与讨论    22
3.1产物形态    22
3.1.1甲基MQ树脂（硅酸钠法）合成实验结果    22
3.1.2甲基MQ树脂（硅酸酯法）合成实验结果    24
3.1.3苯基MQ树脂（硅酸酯法）合成实验结果    24
3.1.4结论    25
3.2苯基MQ树脂的表征（红外分析）    26
3.2.1甲基MQ树脂产物红外谱图分析    26
3.2.2苯基MQ树脂产物红外谱图分析    27
3.3实验中存在的问题    28
4研究结论    29
致谢    30
参考文献    31
附录：设备    33
 1绪论
有机硅材料具有许多优异的性能，现在在各个领域的应用日益广泛，对硅树脂的研究也处在白热化阶段。硅树脂是4 大有机硅材料之一，具有一般有机树脂难以达到的耐高温、耐候性及耐腐蚀性[1]。近年来，有关硅树脂的研究工作进展相当快，一些成果已在工业上得到应用，比如MQ硅树脂主要用作有机硅压敏胶、液体硅橡胶、个人护理品及其它助剂等。 苯基MQ树脂的制备与表征+文献综述:http://www.751com.cn/huaxue/lunwen_14550.html