摘要稀土掺杂碱土铝酸盐类长余辉荧光材料作为一种非放射性荧光粉，具有优良的发光性能，同时生产过程中也不存在环境污染的问题，具有很广阔的应用前景。
本论文系统地总结和概括了稀土离子激活碱土铝酸盐长余辉发光材料的研究现状，采用微波法以及燃烧法对长余辉荧光材料进行制备。首先还原剂对实验过程有很重要的影响，在工艺中，还原剂的多少直接影响到是否能得出产品，因此在反应过程中，还原剂应过量；硼酸的掺入会导致粉体粒径的增大，但同时也能有效改善粉体的长余辉发光性能。602
关键词 碱土铝酸盐，稀土，长余辉，荧光体
毕业设计说明书（论文）外文摘要
Title Synthesis of Persistent Phosphorescent Materials of Aluminate
Abstract
Long lasting phosphorescence of alkaline earth aluminate doped with rare earth as a non-radioactive phosphor has excellent luminescent property and not environmental pollution in the process of preparation,so it has wide application prospect.
Research status for the persistent phosphors of rare earth ions doped alkali earth aluminate was systemically summarized in this paper. We use microwave method and burning method to prepare alkaline earth aluminate long lasting phosphorescence phosphors. At first, the effect of reducing agent is important. In the process, the number of the reducing agent directly affects weather the product can be gotten. Therefore in the reaction process, the reducing agent should be excessive. When mixed with boric acid, the powder particle size will be increased, and long lasting phosphorescence properties can be improved effectively.
Keywords alkaline earth aluminate, rare earth, long lasting phosphorescence, phosphors
目 次
1 引言 1
1．1 长余晖发光材料的介绍 1
1．2 发光材料的特征及种类 1
1.2.1发光材料的特征 1
1.2.2发光材料的种类 1
1.3 长余辉发光材料的种类及特性 2
1.3.1硫化物长余辉发光材料 3
1.3.2铝酸盐长余辉发光材料 3
1.3.3硅酸盐长余辉发光材料 4
1.4 稀土光致发光材料的概况 4
1.5 铝酸盐长余辉材料的制备方法 5
1.5.1 用高温固相反应法 5
1.5.2溶胶-凝胶法 5
1.5.3共沉淀法 5
1.5.4微波法 6
1.5.5燃烧法 6
1.6本课题的研究目的 6
2 实验——制备SrAl2O4: Eu2+, Dy3+ 7
2.1 微波法 7
2.1.1实验药品及器材 7
2.1.2氧化铁与四氧化三铁的比较 7
2.1.3四氧化三铁的制备 7
2.1.4 实验步骤 7
2.1.5 实验原理 8
2.1.6实验问题 8
2.2燃烧法制备 8
2.2.1实验步骤 8
2.2.2实验原理 8
2.3 结果分析与讨论 9
2.3.1 样品晶体结构的测定 9
2.3.2 Eu2+浓度对SrAl2O4: Eu2+, Dy3+ 材料发光性能的影响 10
2.3.3 硼酸的加入量对SrAl2O4: Eu2+,Dy3+ 材料发光性能的影响 11
2.3.4 还原剂对SrAl2O4: Eu2+, Dy3+样品发光性能的影响 13
结 论 15
致 谢 16
参 考 文 献 17 Eu、Dy掺杂碱土铝酸盐长余辉荧光粉体的制备:http://www.751com.cn/huaxue/lunwen_3339.html