摘要利用电镀法制备得到Co-P-B合金催化剂，并把它用于水解硼氢化钠制得氢气。经过适当的程序干燥后的氢气，可以充当质子交换膜燃料电池的氢源。在本论文中，主要介绍了以泡沫Ni为模板，通过电镀法获得Co-P-B催化剂，然后采用控制变量法，通过改变Co-P-B合金的的一些条件，不断优化制得催化性能好的催化剂。通过对水解液的研究，来确定最优的产氢条件。产氢条件的优化，将有助于高效、高速的完成析氢过程。50166

该论文有图35幅，表32个，参考文献6篇

毕业论文关键词： 电镀  Co-P-B  水解  硼氢化钠  

Co-P-B non-noble metal alloy gold catalyst of hydrogen preparation and hydrogen production performance

Abstract

Preparation obtained by plating Co-P-B alloy catalysts, and use it for the hydrolysis of sodium borohydride to obtain hydrogen。After proper drying procedure , it can act as a source of hydrogen proton exchange membrane fuel cell. In this paper, we introduce foam Ni as a template, Obtaining Co-P-D by plating catalyst,then use the control variable method, by changing the Co-P-B alloy of a number of conditions, Continuously optimized to obtain good catalytic performance catalyst. Through the study of hydrolyzate to determine the optimal conditions for hydrogen production. Optimization of hydrogen production will help efficient, high-speed completion of hydrogen evolution.

Key words：plating  Co - P - B  hydrolysis  Sodium borohydride

目录

摘要 I

Abstract II

图清单 V

表清单 VI

1 绪论 1

1.1 发展现状 1

1.2 制氢电极材料 2

1.3 泡沫镍 3

1.4 水解液 3

2 实验内容 5

2.1材料Co-P-B合金准备 6

2.1.1 泡沫镍制备方法 6

2.1.2 电镀Co-P-B 7

3 结果及讨论 8

3.1 实验理论过程 8

3.2 电镀器材的选取 10

3.3 实验优化 10

3.3.1  Ni2+浓度 12

3.3.2  Co2+浓度的不同 14

3.3.3  镍离子浓度的再优化 15

3.3.4  硼酸浓度 16

3.3.5  电镀一EG比重 17

3.3.6  CoCl2浓度 17

3.3.7  CoCl2 浸泡时间 18

3.3.8  CoCl2浸泡液溶剂的配比 19

3.3.9  硼氢化钠浓度 19

3.3.10 氢氧化钠浓度 20

3.3.11 次亚磷酸钠 浓度 21

3.3.12 电镀二 溶剂 22

3.3.13 电镀一电流 23

3.3.14 电镀一 电镀时间 23

3.3.15 电镀一 电镀温度 24

3.3.16 增加部分Fe元素（尝试） 24 CoPB非贵金属合金制氢催化剂的制备及制氢性能:http://www.751com.cn/huaxue/lunwen_53418.html