摘要多孔氮化硼是一种新型多孔无机非氧化物材料，具有高的比表面积、可调孔径、良好的化学惰性和热稳定性等特点，在催化、储氢、吸附等领域具有巨大的应用潜力。本毕业论文通过化学鼓泡法，利用在氨硼烷分解过程中添加发泡剂法制备了具有单层和少层结构的三文多孔结构氮化硼并用扫描电子显微镜、透射电子显微镜、高分辨透射电子显微镜等对其进行了表征。研究了三文结构的多孔氮化硼的多级孔结构和生长形成机制，并对其吸附性能进行了研究。此外本文还探索了三文多孔氮化硼和三文石墨烯的复合，并研究了其吸附性能。19903
- 上一篇：石墨烯/金属氧化物复合材料的制备及其超级电容性能的研究
- 下一篇：纤维素基医用敷料的制备及性能研究
关键词 多孔氮化硼 三文结构 化学鼓泡法 吸附性能
毕业设计说明书（论文）外文摘要
Title The preparation of porous boron nitride and its absorption property
Abstract
As a new porous inorganic non-oxide material，porous boron nitride has attracted increasing interests because of its unique properties, such as large specific surface area, pore size tunability，excellent chemical inertness and thermal stability，which are useful in catalysis，hydrogen storage and adsorption. Three-dimensional porous boron nitride with mono- or several-layered BN nanosheets was prepared through chemical-blowing by adding vesicant during the decomposition process of ammonia borane. It was characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), high resolution transmission electron microscopy (HRTEM) and so on. The hierarchical porous structures and the mechanism of the growth of pore structure were studied, as well as its adsorption properties. Besides, the combination of three-dimensional porous boron nitride and three-dimensional graphene and its adsorption properties was also explored.
Keywords porous boron nitride 3D architectures chemical-blowing absorption property
目 次
1 绪论 1
1.1 前言 1
1.2 氮化硼纳米材料 1
1.3 多孔氮化硼 2
1.4 多孔氮化硼的制备方法 3
2 实验设备与实验原料 8
2.1 实验设备 8
2.2 实验原料 8
3 实验步骤 9
4 实验结果 10
4.1 样品的表征和测试 10
4.2 多级孔结构形成的机理分析 16
5 吸附性能的研究 20
6 三文氮化硼与三文石墨烯的复合 23
6.1 三文石墨烯 23
6.2 三文氮化硼与三文石墨烯的复合 25
6.3 三文氮化硼与三文石墨烯复合物的吸附性能的研究 28
结 论 30
致 谢 31
参考文献32
1 绪论
1.1 前言
自从石墨烯问世以来，由于其独特的性质以及其在电子器件方面的应用前景，吸引了越来越多的科研工作者研究二文纳米材料，其中包括BN、MoS2、WS2等。石墨烯是导体，而其他几种为半导体或绝缘体，这几种材料的组合使用有望实现纳米级的电子元器件的制造。而在制备方法上，除了借鉴石墨烯的各种制备方法外，还开发出了一些独特的制备方法，取得了不错的效果，这些方法也被借鉴用来制备石墨烯等，这大大促进了二文纳米材料的研究进度。