摘要本文采用有限元数值模拟方法研究了不同的衬垫层结构对于热循环下热障涂层(TBCs)应力分布的影响。首先选取高温镍基合金为基体，NiCrAlY为衬垫层，氧化钇稳氧化锆为隔热层。进而建立二文的热障涂层模型，包括传统衬垫结构、理想网状衬垫结构、实际网状衬垫结构、复合衬垫结构，计算在热循环载荷作用下的热障涂层残余应力的分布。结果表明：冷却过程中，传统衬垫结构TBCs中陶瓷层的收缩导致涂层边缘处产生较大横向残余拉应力和纵向残余压应力，形成垂直表面裂纹,容易使涂层在边缘处破碎剥落；理想网格状衬垫结构可以降低边缘处的残余应力，但由于棱角的存在会导致网格衬垫附近产生较大应力集中；依据实际网状衬垫结构将棱角做钝化处理，改善了网格衬垫附近应力集中的状况；在实际网状衬垫层与基体之间加入层状衬垫层，构成复合衬垫结构，可以进一步改善网格衬垫附近应力集中的状况，而且能够提高基体的抗氧化性能。19934
- 上一篇：纤维素基医用敷料的制备及性能研究
- 下一篇：D6AC钢与T2铜熔敷焊接接头的组织性能研究
关键词 热障涂层 有限元法 热循环 残余应力
毕业论文设计说明书（论文）外文摘要
Title Numerical simulation of residual stress field of thermal barrier coatings during thermal cycling
Abstract
In this paper, the finite element numerical simulation method has been used to study the distributions of residual stresses of Thermal Barrier Coatings (TBCs) with different structure during thermal cycling. Firstly, the TBCs have three component: substrate(high temperature Nickel-base Alloy), bond layer(NiCrAlY), insulating layer(Yttria stabilized Zirconia). Then a two-dimensional model of thermal barrier coatings is established，including the traditional structure, the ideal reticular structure, actual reticular structure and composite structure. Finally, the influence of the distributions of residual stresses of TBCs during thermal cycling on the performance of coating is investigated. The results show that the shrinkage of ceramic coating with traditional structure lead to a large horizontal and vertical residual stresses and form a vertical surface cracks at the edge of TBCs. Therefore, TBCs will fracture easily. With ideal reticular structure the residual stresses at edges is reduced. But the prisms of the reticular structure will lead to a strong concentration of stress. The decrease of the sharp shape of ideal reticular structure will improve this situation. Adding a layer between actual reticular structure and substrate can improve the concentration of stress and enhance the capacity of oxidation resistance.
Keywords thermal barrier coatings finite element method thermal cycling residual stress
目 录
1 绪论 1
1.1 热障涂层概述 1
1.2 热障涂层的研究现状 1
1.3 有限元方法及ANSYS软件介绍 7
1.4 本文的主要内容 9
2 具有传统衬垫结构的热障涂层 10
2.1 物理模型 10
2.2 材料参数 11
2.3 边界条件 12
2.4 结果分析 12
3 具有理想网状衬垫结构的热障涂层 16
3.1 物理模型及条件设定 16
3.2 结果分析 16
4 具有实际网状衬垫结构的热障涂层 20
4.1 物理模型及条件设定 20
4.2 结果分析 20
5 具有复合衬垫结构的热障涂层 24
5.1 物理模型及条件设定 24
-
ADS的SIMP系列耐热钢组织结...
-
DZ4125镍基高温合金衬垫结...
-
45钢螺柱-钢板结构摩擦复合热源螺柱焊接研究
-
ANSYS钢铁零件淬火热力学耦合有限元分析
-
高强铝合金螺柱感应+拉弧...
-
厚大构件机器人复合热源...
-
高强钢复合热源螺柱焊螺...
中考体育项目与体育教学合理结合的研究
乳业同业并购式全产业链...
电站锅炉暖风器设计任务书
当代大学生慈善意识研究+文献综述
河岸冲刷和泥沙淤积的监测国内外研究现状
大众媒体对公共政策制定的影响
java+mysql车辆管理系统的设计+源代码
杂拟谷盗体内共生菌沃尔...
十二层带中心支撑钢结构...
酸性水汽提装置总汽提塔设计+CAD图纸