摘要：本文通过以氢氧化锂（LiOH），草酸亚铁（FeC2O4），硼酸（H3BO3），硝酸铬Cr(NO3)3和蔗糖为原料通过球磨、喷雾干燥法成功地合成了LiFeBO3/C，并使用XRD和SEM对其进行表征。SEM分析表明，LiFeBO3/C粉末由粗糙类似球形颗粒尺寸直径约为5μm。电化学性能测试表明，LiFeBO3/C具有高的首次放电比容量和良好的循环性能，0.1C的倍率在1.5V和4.5 V之间的首次放电容量181mAh /g，在10次循环后保持为175mAh/g放电比容量。38620
- 上一篇：Fe-Mn熔体中Mn的活度研究
- 下一篇：PKN晶体的发光性能研究
毕业论文关键词：硼酸铁锂；喷雾干燥；正极材料；电化学性能
Abstract
Abstract ：The LiFeBO3/C has been successfully synthesized via ball milling and spray-drying method using LiOH, FeC2O4, H3BO3, Cr(NO3)3and Sucrose as starting materials. The samples were characterized by X-ray diffraction and scanning electron microscopy. SEM analysis shows that the size of the LiFeBO3/C powder is about 5 μm with the size of the spherical particles. Electrochemical test of materials show that LiFeBO3/C exhibited a higher discharge mass specific capacity and good cycle stability. The prepared LiFeBO3/C presents an initial discharge capacity of 181mAh/g at 0.1C between 1.5 and 4.5 V, and it can deliver a discharge capacity of 175 mAh/g after 10 cycles.
Key Word：Lithium iron borate；Spray-drying； Cathode material ；Electrochemical properties
目 录
1 引言 1
1.1 锂离子电池 1
1.1.1 锂离子电池发展史 1
1.1.2 锂离子电池工作原理 1
1.2 锂离子电池优缺点 2
1.2.1 锂离子电池的优点 2
1.2.2 锂离子电池的缺点 3
1.3 锂离子电池的现状 3
1.4 常见锂离子电池正极材料 3
1.4.1 LiMn2O4 3
1.4.2 LiCoO2 4
1.4.3 LiFePO4 4
1.4.4 LiFeBO3 4
1.5 锂离子电池正极材料的各种制备方法 6
1.5.1 固相反应 6
1.5.2 共沉淀法 6
1.5.3 水热法 6
1.5.4 溶胶-凝胶法 7
2 实验部分 8
2.1 实验方案 8
2.2 实验材料与仪器 8
2.2.1 实验材料 8
2.2.2 实验仪器 8
2.3 实验过程 9
2.3.1 样品制备 9
2.3.2 电极片的制作 10
2.4 LiFePO4与LiFeBO3的表征 10
2.4.1 物相分析 10
2.4.2 微观形貌 10
2.5 电化学性能测试 10
2.5.1 充放电测试 10
2.5.2 循环伏安测试 10
3 实验结果与分析 11
3.1 不同煅烧温度对LiFeBO3的影响 11
3.2 不同保温时间对LiFeBO3的影响 14
3.3 不同倍率对LiFeBO3的影响 19
3.4 结论 21
展望 22
致谢 23