摘要本论文以2mm的TA1与6mm的Q235B及2mm的TA1三层爆炸复合板材为对象，开展了脉冲熔化极气体保护焊和钨极氩弧焊的焊接方法的研究。 设计了坡口形式并优化了焊接工艺参数，利用优化的工艺参数进行钛钢钛三层爆炸复合板的拼接实验，获得了成型良好的多层焊缝，并对母材和试样进行了微观金相组织的观察与显微硬度测试以及电镜扫描。67489
研究表明: 无论是爆炸焊缝与对接焊缝，焊缝界面都有着显微硬度的升高，随着与界面的距离增加，硬度逐渐回复到本身材质的硬度大小。
爆炸焊缝与对焊焊缝周围的钛铁元素均发生了少量的扩散。对于对焊来说，焊缝区的热输入最大，再从中心到两边递减，这使得钛铁的扩散也就从中心到两边减小。但是无论是母材还是式样，钛的元素强度总是稍微大于铁元素的强度。
毕业论文关键词 钛钢钛爆炸复合板 熔化极气体保护焊 钨极氩弧焊 焊缝成型 金相组织
毕业设计说明书（论文）外文摘要
Title Butt-joint Welding Process of the Explosion Welding Ti-Steel-Ti Composite Plates
Abstract
This thesis with 2 mm TA1 and Q235B of 6 mm and 2 mm of TA1 three layers of explosive composite sheet as an object, has carried out pulse melting polar gas shielded arc welding and tungsten electrode argon arc welding welding method of the research. Design and optimize the technological parameters of welding groove form, the use of optimization of process parameters for titanium steel titanium three experiments, the joining together of explosive composite board forming good multilayer weld, and the sample material and microscopic observation of microstructure and micro hardness testing and scanning electron microscope.
Research has shown that both explosion welding and butt weld, the weld interface has a microhardness increases, with increasing distance and interface, the hardness gradually return to itself the hardness of material size.
Explosion welding and butt weld titanium iron are happened around a small amount of diffusion. For butt weld, the heat input is the largest, and from center to both sides, which makes the spread of the titanium iron also decreased from center to both sides. But neither parent metal or styles, titanium element strength is slightly greater than the strength of the iron.
Keywords Ti-Steel-Ti composite plates of explosion welding MIG welding TIG welding appearance of weld metallographic organization
目录
1 绪论 1
1.1选题背景及意义 1
1.3爆炸复合材料应用前景和市场预测 2
1.4复合板焊接特性分析 3
1.4.1 钛与钢异种金属的焊接 3
1.4.2 工业纯钛的焊接特性 3
1.5本论文研究内容 4
2 试验材料、设备及方法 5
2.1试样材料及焊接材料 5
2.2焊接设备的选择 5
2.2.1 脉冲熔化极气体保护焊 5
2.2.2钨极氩弧焊 7
2.4硬度测试仪 9
2.5 EDAX电镜扫描仪 10
3 焊接过程 12
-
硬模板法制备纳米级二氧...
-
钛合金激光+PMIG对接焊工艺...
-
铝镁复合板的爆炸焊及扩散焊焊接工艺研究
-
微量元素对钛铝合金微观组织的影响
-
纯钛表面纳米化及其生物活性的研究
-
钛钢爆炸复合板机器人拼接工艺研究
-
钛合金薄壁筒体及挂件PMIG焊接工艺试验研究
中考体育项目与体育教学合理结合的研究
酸性水汽提装置总汽提塔设计+CAD图纸
乳业同业并购式全产业链...
十二层带中心支撑钢结构...
当代大学生慈善意识研究+文献综述
电站锅炉暖风器设计任务书
大众媒体对公共政策制定的影响
杂拟谷盗体内共生菌沃尔...
河岸冲刷和泥沙淤积的监测国内外研究现状
java+mysql车辆管理系统的设计+源代码