摘要本文主要针对在铝基体上采用钢焊丝+铝镁焊丝获得铁铝堆焊层，通过调节焊接工艺参数，使Fe-Al堆焊层成形良好，无气孔、裂纹、夹杂等缺陷出现，使Fe-Al合金主要成分为Fe3Al。
铁铝堆焊的焊缝以柱状晶存在，且其中含有大量的析出相，当钢焊丝的送丝速度为8m/min,铝焊丝的送丝速度为4.5m/min时，焊缝成形良好，硬度在370HV左右，与Fe3Al化合物的硬度很接近，说明焊缝层中存在Fe3Al。67488
毕业论文关键词： Fe-Al堆焊层，双丝焊工艺，显微组织，硬度
毕业设计说明书（论文）外文摘要
Abstract This article mainly aims at on the aluminum substrate by using steel wire + aluminum magnesium iron wire for hardfacing layer, by adjusting the welding process parameters, make the Fe - Al surfacing layer forming good, without defects such as porosity, crack, inclusion, the main ingredients of Fe3Al Fe - Al alloy.
Iron and aluminum welding the weld to the existence of the columnar crystal, and contains a large number of precipitated phase, when the steel wire of the wire feeding speed is 8 m/min, weld wire wire feed speed of 4.5 m/min, the weld is good, the hardness is controlled in 370 hv, and the hardness of Fe3Al compounds is very close to that of weld layers exist in the Fe3Al.
Keyword:Fe-Al surfacing layer, double wire welding process, the microstructure and hardness
1绪论 6
1.1 本课题的研究意义和内容 6
1.1.1 本课题的研究意义 6
1.1.2本课题的研究内容 6
1.2 Fe-Al 金属间化合物研究概况与发展方向 6
1.2.1 Fe-Al金属间化合物室温脆性本质 6
1.2.2 合金化 7
1.3 Fe-Al合金层的制备方法和局限性 7
1.3.1高速电弧喷涂技术 7
1.3.2 激光熔敷技术 7
1.3.3 等离子喷涂技术 8
1.4 双丝焊分类及其特点 8
1.4.1 双丝焊的研究状况 8
1.4.2 双丝焊的优点及其应用 9
2 铝钢异种金属双丝焊试验设备及材料 10
2.1 法国SAF公司的R450双丝焊机工作原理 10
2.2 实验设备 11
2.2.1 法国SAF公司的双丝焊接系统双丝焊焊接系统组成 11
2.2.2 金相显微境 12
2.3 试验材料 13
2.3.1 母材 13
2.3.2 焊丝牌号 13
2.3.3 保护气体 13
3 试验方案设计及分析 14
3.1 焊接操作过程 14
3.2 试验结果 14
4 金相实验 16
4.1 金相实验步骤 16
4.2 试样宏观分析 16
4.2.1 5mm铝板表面堆铁铝 16
4.2.2 5mm铝板表面堆铁后，再堆铁铝