摘要本文研究了不同方法制备的铈钨复合氧化物催化剂NH3-SCR反应活性，通过对制备过程中不同影响因素的调试，确立了最优的催化剂制备条件。结果表明，采用优化后的直接蒸干法制备的CeWOx催化剂在很宽的温度窗口(150℃～450℃)范围内具有优异的NOx去除率和N2选择性，且其催化性能明显优于已经工业化应用的V2O5/WO3-TiO2催化剂，具有广阔的应用前景。采用方法更加简易的固体研磨法制备的CeWOx催化剂同样具有良好的NH3-SCR反应活性。Ce和W的协同作用是CeWOx催化剂具有优异催化性能的可能原因。21111
- 上一篇：硝酸条件下不锈钢+碳钢材料缓蚀剂的开发研究
- 下一篇：硝仿肼的包覆改性研究+文献综述
关键词 选择性催化还原 CeWOx 制备方法 NOx转化率
毕业论文设计说明书（论文）外文摘要
Title Improvement and Development of the Vanadium-based Oxide NH3-SCR Catalysts
Abstract
In this study, cerium-tungsten oxide catalysts were prepared by different methods and investigated for selective catalytic reduction of NOx with NH3 (NH3-SCR) performance. Optimal conditions for preparing the catalyst were established by ameliorating different factors of the preparation processes. The results showed that, the direct drying of the CeWOx catalyst resulted in excellent NOx conversion and N2 selectivity in the broad temperature range of 150℃～450℃, and showed much better SCR performance than V2O5/WO3-TiO2 catalysts, which have been industrially and commercially applied for NOx abatement. The catalysts prepared by the solid process methods exhibited great SCR activity as well. The excellent catalytic activity of CeWOx catalyst was possibly caused by the synergetic interaction among the Ce and W species.
Keywords Selective catalytic reduction CeWOx Preparation methods
NOx conversion
目 次
1 引言 1
1.1 氮氧化物的危害与来源 1
1.2 NH3-SCR技术 1
1.3 NH3-SCR催化剂研究现状 2
1.4 课题的提出与内容 5
2 实验部分 6
2.1 实验室仪器与试剂 6
2.2 实验内容 7
3 结果与讨论 11
3.1 铈钨氧化物催化剂制备方法的初步探究 11
3.2 直接蒸干法制备铈钨氧化物催化剂的研究 13
3.3 铈钨氧化物催化剂制备方法的进一步探索 17
结 论 21
致 谢 22
参考文献 23
1 引言
1.1 氮氧化物的危害与来源
氮氧化物（NOx，通常包括NO和NO2）是大气中一种主要的污染物，在绝大部分大气变化过程中起到重要的影响作用[1]。NOx具有较强的生物毒性，直接危害人体的呼吸系统[2]。同时，NOx的超量排放还会带来光化学烟雾、酸雨、温室效应、臭氧层破坏等一系列生态环境问题[7,8]。
大气中NOx的来源主要分为两方面——自然源和人为源。自然来源由微生物代谢、雷电、火山喷发等产生；人类活动排放的NOx包括两个途径，农业生产和燃料燃烧。由于过量使用化石燃料，致使人为排放的NOx早已超过自然排放量[2]。以燃煤电厂为代表的固定源NOx排放和以柴油车尾气为代表的移动源NOx排放，是大规模开发和利用化石燃料主要的氮氧化物人为排放源。人类活动所产生的NOx多集中于城市、工业区等人口稠密地区，对人体的健康危害较大。因此，如何有效地控制NOx的排放，是目前我国治理空气污染行动中亟待解决的关键问题。