    摘要:本课题主要研究了包覆UVA/UVB防晒剂固体脂质微粒的影响因素，研究了添加剂对固体脂质微粒的影响，实验结果表明随着添加剂用量增加，其粒径不断增大，对分散性影响较小；通过对响应面实验制备工艺的研究，得出当超声时间为14.57分钟，超声功率756.25W，乳化温度87.92℃时为最优的制备工艺。考察了防晒剂的含量对固体脂质微粒的影响，并分析了其紫外吸收特性，选择防晒剂甲氧基肉桂酸辛酯（OMC）的加入量为5%，丁基甲氧基二苯甲酰甲烷（BMBM）加入量为2%；通过考察配方组成对体系粒径和分散系数的影响，得到最优配方为辛酸癸酸三甘油酯（GTCC）加入量为3.01%，氢化蓖麻油加入量为2%、鲸蜡硬酯基醚-20加入量为10%；并对包覆防晒剂的固体脂质微粒的表征进行了分析，进行了部分稳定性测试，发现固体脂质防晒粒在高温下有较好的稳定性。24736
    毕业论文关键词：防晒剂；固体脂质微粒；表征；稳定；
    The Study of the Effect Factors of the Solid Lipid Sunscreen Particles Loaded UVA/UVB Sunscreen
    Abstract：In this study, the effect factors of UVA/UVB sunscreen-coated solid lipid sunscreen particles were studied. After studying the effect of additives of solid lipid particles, the experimental results show that with the increase of the amount of additives, the particle size increasing and less influence on its distribution; Through the study of preparation technology based on response surface experiment, it is concluded that when the ultrasonic time was 14.57 minutes, ultrasonic power was 756.25W and emulsifying temperature was 87.92℃, the preparation process is optimal. The amount of sunscreen on the influence of the solid lipid particles, and the ultraviolet absorption characteristics was analyzed, then the dosage of sunscreen octylmethoxycinnamate（OMC）and butyl methoxydibenzolymethane（BMBM）were 5% and 2%, respectively by the study of formulation composition which effect on the influence particle size and dispersion, its optimal formulation was composed of Caprylic/Capric Triglyceride（GTCC）3.01%, Castor Oil Hydrogenated 2% and Ceteareth-20 10%. Meanwhile, the solid lipid particle coated with sunscreens were characterized and the stability was researched. The result showed that solid lipid sunscreen hads good stability at high temperature.
    KeyWords：sunscreen; solid lipid particle; characterization; stability；
     目  录
    1 绪论    1
    1.1本课题国内外研究现状概述    1
    1.2 防晒化妆品    1
    1.3 固体脂质微粒    2
    1.4固体脂质微粒的制备    3
    1.5 固体脂质微粒的应用    4
    1.6课题的研究目的和意义    6
    2 实验内容    8
    2.1 实验原料与设备    8
    2.1.1实验原料    8
    2.1.2 实验所用设备    8
    2.2 实验方法    9
    2.2.1样品的制备方法    9
    2.2.2 固体脂质微粒的形态    9
    2.2.3 固体脂质防晒粒的粒径大小及分布的测定    10
    2.2.4紫外吸光度的测定方法    10
    2.2.5 DSC差示扫描量热法    10
    2.2.6 固体脂质微粒的稳定性测定    10
    3 实验结果与讨论    11
    3.1添加剂对固体脂质微粒的影响    11
    3.1.1 甘油对固体脂质微粒的影响    11
    3.1.21,2-丙二醇对固体脂质微粒的影响    12
    3.1.3 1,3-丁二醇对固体脂质微粒的影响    12
    3.2 工艺优化响应面实验    13
    3.3液态防晒剂对固体脂质微粒的影响    17
    3.3.1甲氧基肉桂酸辛酯OMC对固体脂质微粒的影响    17
  1. 上一篇：纳米乳状液包埋柠檬醛的技术研究
  2. 下一篇：一种3－甲基－环十五烯酮反应设备的设计

  1. 含能聚合物包覆超细铝粉复合粒子的制备

  2. 环糊精包覆香精的热解特性研究

  3. 纳米Fe3O4包覆凹土复合吸附剂的合成及性能

  4. 固体脂质微粒包覆二氧化钛的制备技术研究

  5. 包覆精油的脂质体制备技术研究

  6. 聚丙烯酸酯包覆桂花香精胶囊的制备

  7. PPY包覆的LiMnO4纳米阵列用于柔性锂离子电池

  8. 十二层带中心支撑钢结构...

  9. 电站锅炉暖风器设计任务书

  10. 河岸冲刷和泥沙淤积的监测国内外研究现状

  11. 当代大学生慈善意识研究+文献综述

  12. 杂拟谷盗体内共生菌沃尔...

  13. 中考体育项目与体育教学合理结合的研究

  14. 乳业同业并购式全产业链...

  15. 大众媒体对公共政策制定的影响

  16. 酸性水汽提装置总汽提塔设计+CAD图纸

  17. java+mysql车辆管理系统的设计+源代码

　　

About

751论文网手机版...

主页：http://www.751com.cn

关闭返回