摘要：以TAA，SnCl25H2O为原料，PVP为形貌修饰剂，通过低温水热法合成了SnS2纳米颗粒，并利用X射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜（TEM）、高分辨透射电子显微镜(HRTEM)、紫外-可见漫反射光谱(UV-vis)对其进行了元素分析、形貌分析、光学分析。随后，以重铬酸钾标准液作为含Cr(VI)离子的污水模型，考察了所得纳米材料对Cr(VI)离子光还原的催化活性。此外，还系统研究了反应条件对Cr(VI)离子光催化还原效率的影响。最终得到了制备具有高光催化活性SnS2的工艺条件。48230
毕业论文关键词：SnS2，水热法，Cr(VI)离子，光催化
Preparation of sulfur containing nano materials
Abstract：Through the low temperature hydrothermal method，used the TAA and SnCl25H2O as raw materials,the PVP as morphology modifier. Then used XRD, SEM, TEM, HRTEM, UV-vis to do the elemental analysis, morphology analysis and optical analysis.After that , with standard potassium dichromate solution as Containing Cr(VI) ions in the sewage treatment model, the effects of the obtained nano materials of Cr(VI) ion photoreduction of catalytic activity. In addition, the effect of reaction conditions on the photocatalytic reduction efficiency of Cr(VI) ions was also studied. The process conditions for the preparation of SnS2 with the highest photocatalytic activity were obtained.
Key word：SnS2 hydrothermal Cr(VI) photocatalysis
目录
1绪论 １
1.1 引言 １
1.2 SnS2纳米材料 ２
1.3 水热合成法合成纳米材料 ２
1.4 增强半导体纳米材料光催化活性的主要方法 ３
1.4.1形貌调控法 ３
1.4.2 晶面调控法 ４
1.4.3 复合合成（异质结构） ４
1.5含有Cr(VI)污水的治理 ４
1.6本课题的研究目的与意义 ５
2 实验药品、实验仪器及实验方法 ６
2.1.1 实验试剂 ６
2.1.2 实验仪器 ６
2.2实验部分 ６
2.2.1 SnS2（二硫化锡纳米颗粒）的制备 ６
2.2.2 Cr(VI)母液的配制 ７
2.2.3 二苯碳酰二肼溶液的配制 ７
2.2.4对含六价铬水溶液的光催化降解实验 ７
3.1 二硫化锡纳米粒子的晶相分析 ９
3.2二硫化锡纳米粒子的元素分析 １０
3.3二硫化锡纳米粒子的形貌分析 １１
3.4二硫化锡纳米粒子的光学性质 １２
3.5二硫化锡纳米粒子的光催化降解分析 １３
3.5.1 暗吸附曲线 １３
3.5.2 光催化动力学曲线 １４
3.5.3 PVP用量对光催化活性的影响 １４
3.5.4 水热温度对光催化活性的影响 １６
3.5.5 水热时间对光催化活性的影响 １７
3.6光催化机理的初步探讨
-
ANSYS微推进器阵列低温键合...
-
低游离聚氨酯预聚体与传...
-
水热法制备氮掺杂石墨烯-片状Co(OH)2复合材料
-
溶剂热法制备氮掺杂石墨烯-Cu纳米复合材料
-
水热法合成石墨烯-普鲁士蓝复合材料
-
低放稀土酸溶渣放射性处理与处置初探
-
新型低燃温气溶胶灭火剂技术研究
当代大学生慈善意识研究+文献综述
河岸冲刷和泥沙淤积的监测国内外研究现状
十二层带中心支撑钢结构...
电站锅炉暖风器设计任务书
乳业同业并购式全产业链...
酸性水汽提装置总汽提塔设计+CAD图纸
杂拟谷盗体内共生菌沃尔...
中考体育项目与体育教学合理结合的研究
java+mysql车辆管理系统的设计+源代码
大众媒体对公共政策制定的影响