摘要使用不同含量的三元树脂作为扩链剂，与聚醚多元醇、IPDI反应合成聚醚聚氨酯，通过使用DMA测试、AFM原子力测试、拉伸试验、红外光谱测试对合成的聚醚聚氨酯增强体系进行性能研究。结果表明：随着扩链剂三元树脂含量的增加，聚醚聚氨酯材料的耐低温性能有较大提高，断裂伸长率、拉伸应力性能提高显著，材料的表面性能有明显改善。同时还对不同含量的改性碳纤维作为增强剂的聚氨酯体系进行以上测试，得出相关结论。63849
毕业论文关键词 聚醚聚氨酯；扩链剂；力学性能；三元树脂；改性碳纤维。
毕业设计论文外文摘要
Title Mechanical properties of polyether polyurethane systems
Abstract Ternary content using different resin as a chain extender, and a polyether polyol, IPDIpolyether polyurethanes synthesized, by using the DMA test, AFM Atomic Force test, tensile test, the infrared spectra of the synthesized polyether polyurethane system forenhanced performance. The results showed that: a chain extender with three yuan resin content increases, the polyether polyurethane materials have greatly improved low temperature properties, elongation, tensile stress significantly improved performance,materials, surface properties are significantly improved. But also on the different contents of the modified carbon fiber as a reinforcing agent for polyurethane systems above test,draw relevant conclusions.
Keywords Polyether-polyurethanes; chain extender; mechanical properties; three yuan resins; Modified Carbon Fiber.
目录
1 引言 1
2 原料与工艺 2
2.1原料简介 2
2.2仪器设备简介 5
2.3反应工艺 5
2.4反应原理 6
2.4.1聚醚聚氨酯合成原理 6
2.4.2聚氨酯的反应合成方程式 7
2.4.3异氰酸酯的亲核反应机理 7
2.4.4本实验详细机理 8
2.5反应产物 8
3 傅立叶变换红外光谱分析 9
3.1实验仪器参数及条件 9
3.2结果及分析 9
4 动态热机械分析 11
4.1实验仪器及参数 11
4.2结果及分析 12
5 聚氨酯增强体系拉伸试验 16
5.1实验仪器及参数 16
5.2试样及分析 17
6 聚氨酯体系的AFM原子力表征 22
6.1实验仪器和参数 22
6.2结果及分析 23
结论 25
致谢 26
1 引言
聚氨酯是世界六大最具发展前途合成材料之一，由于聚氨酯材料的性能优良，应用范围广，很受欢迎。本实验的聚氨酯弹性体是一种(AB)n型的嵌段共聚物，由线性硬链段IPDI，和扩链剂三元树脂，线性软链段聚醚多元醇组成。聚氨酯弹性体由一种特殊的化学结构，柔性链段，刚性链段以及形成的微相分离是的其综合性能特殊，有较好的优越性：较高的弹性和强度、较宽广的硬度范围、优异的耐磨性、耐油耐水耐溶剂优良、耐低温性优良。异氰酸酯IPDI中—NCO基与聚醚多元醇中的—OH基通过反应形成聚氨酯。聚醚聚氨酯通过这些化学键相互交联成网络体系，该网络体系通过预聚法和一步法进行合成。本实验采用的是聚醚多元醇为主要网络结构，以IPDI为固化剂，三元树脂为扩链剂，生成网络结构，催化剂则采用三苯基铋。聚氨酯合成过程中，IPDI和羟基的反应一直存在，IPDI和羟基进行氢转移，由羟基中亲核中心袭击IPDI基团中的亲电中心形成，反应在较活泼的—NCO基上进行，羟基中氢原子转移到IPDI基团中的氮原子上，余下的基团与羰基碳原子结合，形成氨基甲酸酯[1~3]。论文网