摘要本课题首先采用液-液界面法合成了Bi2S3纳米晶, 通过改变反应时间、反应浓度、反应体积配比、溶剂种类等探讨了反应条件对产物微观形貌的影响。其次采用低温湿化学法法制备了SnS。并采用XRD、TEM、SEM、紫外-可见光谱、红外光谱等对产物结构进行了表征。在实验中，采用黄原酸铋为原料，通过水-氯仿液液界面法制得了类似高粱穗状的Bi2S3纳米晶，改变反应物浓度可得到Bi2S3薄膜，在甲苯-水体系中制备得到了片状Bi2S3纳米晶。5651
关键词 Bi2S3 SnS 纳米晶液-液界面法
Title Bi2S3 nanocrystalline at room temperature of the synthesis and characterization of controllable
Abstract This paper firstly used liquid-liquid surface method to fabricate Bi2S3 nanocrystal. The impact on the morphorlogy of the product was discussed by changing reaction time, reaction concentration, reaction volume ration, types of reagents, and so on. Secondly, we used low temperature wet chemistry method to produce SnS. The structure of the product was characterized by XRD, TEM, SEM, UV-VIS, IR, etc.
    In the experiment, we used the bismuth xanthate as a reactant to form Ears of sorghum -like Bi2S3 nanocrystals by the water-chloriform liquid-liquid surface method. Bi2S3 was obtained by changing the concentration of the reactants. Flake Bi2S3 nanocrystals was formed in the system of toluene and water.
Key words Bi2S3 SnS micro nanocrystalline liquid-liquid interface method
目次
1 引言   1
1.1纳米材料及半导体材料简介   1
1．2 半导体纳米材料的研究   2
1.2.1半导体材料的物理特性   2
1.2.1 .1 小尺寸效应   2
1.2.1.2   量子尺寸效应   2
1.2.1.3 宏观量子隧道效应   3
1.2.1.4   表面效应   3
1.2.1.5 介电限域效应   3
1．3 Bi2S3及SnS的结构与性质简介   4
1.3.2 硫化铋的研究概况   4
1.3.2 硫化亚锡的研究概况   4
1．4 纳米材料的合成与制备方法   6
1.4.1 溶胶-凝胶法   6
1.4.2 离子液法   7
1.4.3 水热/溶剂热法   7
1.4.4 微乳液法   8
1.4.5 液液界面法   8
1.4.6 超声电化学法   9
2 液-液界面法制备Bi2S3纳米晶   10
2.1研究方法概述   10
2.2实验部分   10
2.2.1实验药品及仪器   10
2.2.2 制备   11
2.3 结果分析   11
2.3.1 XRD测试   11
2.3.2反应物浓度对产物形貌的影响   12
2.3.2.1 UV-Vis吸收光光谱   12
2.3.2.2 SEM表征   13
2.3.2.3   TEM表征   14
2.3.2.4 Bi2S3的衍射花样   14
2.3.3反应时间对产物形貌的影响   15
2.3.3.1实物照片   15
2.3.3.2   TEM表征   16
2.3.4溶剂种类对产物形貌的影响   17
2.4本章小结   17
3 SnS 纳米晶的制备   18
3.1实验部分   18
3.1.1实验药品及仪器   18
3.1.2   SnS的制备步骤   18
3.2结构表征   19 室温下Bi2S3纳米晶的可控合成及其表征:http://www.751com.cn/cailiao/lunwen_2773.html