摘要：本课题主要针对工业上一种专用散热器进行扩散连接工艺技术研究。该 散热器由多层316L 不锈钢构成，尺寸为70mm×50mm×0.4mm，片数约为50片。要 求一次焊成，并能承载25MPa 以上水压。根据生产要求，要求进行相关夹具设计， 研究连接温度、压力、连接时间等参数对接头质量的影响等，以获得可靠的焊接 接头。68483

毕业论文关键词 不锈钢 扩散焊

Title Diffusion bonding of multilayer structures dedicated

Abstract

The main topic of diffusion research on industrial connection technology for a special radiator. The multilayer 316L stainless steel sink, the size of 70mm × 50mm × 0.4mm, the number of pieces of about 50. Requires a welded, and can carry more than 25MPa pressure. According to production requirements, and other related requirements affect fixture design, research junction temperature, pressure, time and other parameters of the joint connection quality to obtain reliable welded joints.

Keywords  stainless steel  diffusion bonding

目 次

1.绪论 5

1.1  奥氏体不锈钢焊接方法 5

1.1.1 手工焊(MMA) 5

1.1.2 MIG/MAG 焊接 6

1.1.3 TIG 焊接 6

1.1.4.奥氏体不锈钢的焊接工艺 6

1.2.奥氏体不锈钢的焊接特性 9

1.2.1.晶间腐蚀 9

1.2.2.热裂纹 10

1.2.3.焊接接头的脆化 11

1.3 扩散焊 11

1.3.1 常规扩散焊 (DB) 12

1.3.2  液相界面扩散焊( LID) 12

1.3.3 瞬间液相扩散焊(TLP) 12

1.3.4  超塑成形／扩散连接技术( SPF／DB) 13

1.3.5 扩散焊接的参数 13

2  实验材料、设备及方法 15

2.1 真空扩散焊机工作机理 15

2.2 实验设备 15

2.3 实验材料 17

2.4 实验方法 17

3  硬度测试 17

4 强度分析 18

5 金相分析 18

5.1 宏观组织 19

5.2 微观组织 19

6  实验结果分析 21

结 论 22

致 谢 23

参 考 文 献 24

1.绪论

扩散焊接压力较小,工件不产生宏观塑性变形，适合焊后不再加工的精密零件。 扩散焊可与其他热加工工艺联合形成组合工艺,如热耗-扩散焊、粉末烧结-扩散焊和 超塑性成形-扩散焊等。这些组合工艺不但能大大提高生产率，而且能解决单个工艺 所不能解决的问题。如超音速飞机上各种钛合金构件就是应用超塑性成形-扩散焊制 成的。扩散焊的接头性能可与母材相同，特别适合于焊接异种金属材料、石墨和陶瓷 等非金属材料、弥散强化的高温合金、金属基复合材料和多孔性烧结材料等。扩散焊 已广泛用于反应堆燃料元件、蜂窝结构板、静电加速管、各种叶片、叶轮、冲模、过 滤管和电子元件等的制造。 316L不锈钢多层专用结构扩散连接工艺技术研究:http://www.751com.cn/cailiao/lunwen_77026.html