摘要：本课题研究经过表面改性的纳米粒子对有机硅封装材料性能的影响，分为改性二氧化硅纳米填料与改性P95纳米填料，按照一定的比例混合后，形成透光率高，折射率高，力学性能好的聚合体。使其在大功率LED上满足使用需求。本论文采用苯基硅树脂为原料，在固化的过程中添加入纳米粒子，利用氯铂酸催化剂进行催化固化，并对固化产物进行透光率、折射率等光学和电学性能测试。37091
毕业论文关键词： LED封装；表面改性；纳米复合材料
Modified nanoparticles (SiO2) for LED Packaging
Abstract：The research surface-modified nanoparticles of silicone encapsulating material impact on the performance of the modified silica nano-filler into P95 and modified nanofiller, according to a certain proportion of mixed to form a high transmittance, refractive index high, good mechanical properties of polymers. To meet the demand for the use in high-power LED. In this thesis, phenyl silicone resin as raw material, add Runa Mi particles during the curing process, the use of chloroplatinic acid catalyst catalytic curing, and the cured product was light transmittance, refractive index of the optical and electrical performance testing.
Keywords： LED package; surface modification; nanocomposite
目录
1 绪论    1
1.1  课题研究目的及意义    1
1.2  LED封装用有基硅橡胶纳米复合材料概述    1
1.3  有机硅树脂概述    3
1.3.1 LED封装用苯基硅橡胶纳米复合材料的应用    3
1.3.2 有机硅树脂的性能    4
1.3.3 有机硅封装材料的特点    5
1.3.4 纳米填料改性    6
2 实验部分    8
2.1 实验原料    8
2.2 主要仪器和设备    8
2.3 纳米填料表面处理    9
2.4 纳米粒子改性有机硅复合材料样品配方    9
2.5 制备工艺    10
2.6 结构表征与性能测试    10
2.6.1 红外光谱测试    10
2.6.2 紫外-可见分光光度计    10
2.6.3 介电性能测试    10
2.6.4 电阻率测试    11
2.6.5 导热系数测试    11
2.6.6 扫描电镜测试    11
2.6.7 折射率    11
3 实验结果与讨论    12
3.1 纳米填料偶联剂改性效果的分析    12
3.1.1 偶联剂改性二氧化硅纳米粒子的FT-IR表征与分析    12
3.1.2 偶联剂改性P95纳米粒子的FT-IR表征与分析    13
3.2  纳米粒子对苯基硅橡胶力学性能的影响    13
3.3  纳米填料对甲基苯基硅橡胶电性能的影响    17
3.3.1 纳米填料对甲基苯基硅橡胶介电性能的影响    17
3.3.2 纳米填料对甲基苯基硅橡胶体积电阻率的影响    19
3.4  纳米填料对苯基硅橡胶光学性能的影响    20
3.4.1 纳米填料对苯基硅橡胶折射率的影响    20
3.4.2 纳米填料对甲基苯基硅橡胶透光率的影响    23
3.5  纳米填料硅橡胶复合材料的扫描电镜分析    26
4 结论    27
致谢    28
参考文献    29
1 绪论
1.1  课题研究目的及意义
本项目研制一种高折射率和高热稳定性的有机硅封装材料，该材料具备较好的介电性能和机械性能。通过加入经改性的纳米粒子（SiO2与P95），按照一定的比例混合后，形成透光率高，折射率高，力学性能好的复合材料[1]。使其在大功率LED上满足使用需求。 改性纳米粒子(SiO2P95)对LED封装用有机硅橡胶的性能研究:http://www.751com.cn/cailiao/lunwen_35768.html