摘要本论文探究了氯离子、碳酸根离子、对M5新型抽油杆用钢的腐蚀效果和及其规律性。本文以宝钢特钢有限公司开发的新型抽油杆用钢M5为研究对象，利用电化学工作站、光学显微镜对M5新型抽油杆用钢在腐蚀过程中的极化反应和表面结构进行表征分析。着重利用电化学-极化曲线探讨了M5新型抽油杆用钢的腐蚀机理。结果表明：当氯离子浓度为0.5mol/L时，腐蚀严重；并且表明M5新型抽油杆用钢是抗碱性低碳钢。而研究的碳酸根影响下影响下腐蚀不严重而且还会出现钝化以及过钝化现象。而碳酸根腐蚀属于原电池类，去氢极化机理。氯离子的腐蚀机理属于氧化-还原反应类型。43137
毕业论文关键字：M5新型抽油杆用钢；氯离子腐蚀机理；极化曲线
Abstract
This paper explores the chloride ion and carbonate ion, a new type of M5 steel used for sucker rod corrosion effect and its regularity. Baosteel Special Steel Co., Ltd. to develop new type of pumping rod steel M5 is the main research object by using an electrochemical workstation and optical microscopy of M5 model sucker rod steel in corrosion process of polarization responses and the surface structure were characterized and analyzed. The corrosion mechanism of M5 new type of oil pumping rod is discussed by using the electrochemical polarization curve. The results show that when the chloride ion concentration is 0.5mol/L, the corrosion is serious, and the M5 new type of steel is used as the anti alkali and low carbon steel. But under the influence of carbonate belong to the original battery, hydrogen polarization mechanism. The corrosion mechanism of chloride ion is a kind of redox reaction.
Key words: M5 new type steel of Sucker rod；Cl- corrosion mechanism；Polarization curve
目录
1 绪论 1
1.1 抽油杆用钢 1
1.1.1 抽油杆用钢的概况 1
1.1.2 抽油杆用钢的种类及特点 1
1.1.3 M5新型抽油杆用钢的基本情况 2
1.2 抽油杆用钢的腐蚀机理 3
1.2.1 抽油杆用钢的腐蚀环境 3
1.2.3 抽油杆的腐蚀形式 4
1.3 腐蚀机理研究方法 7
1.3.1 电化学极化曲线实验方法 7
1.3.2 极化曲线分析 8
1.4 选题思路 10
1.5 课题研究的内容 10
1.6 课题实施的技术路线 10
2 实验部分 12
2.1 实验原料及实验仪器 12
2.2 实验过程 13
2.2.1 实验试样的准备与处理 13
2.2.2 实验溶剂的配置 13
2.2.3 电化学工作站的搭桥 14
2.3 表征手段 15
2.3.1 光学显微镜 15
2.3.2 电化学工作站 15
3 结果与讨论 17
3.1 M5抽油杆用钢的组织 17
3.2 氯化钠对M5新型抽油杆用钢的影响 17
3.2.1 不同浓度下氯离子的影响 M5新型抽油杆用钢氯离子腐蚀机理研究:http://www.751com.cn/cailiao/lunwen_43824.html