摘要采用原位聚合的方法制备了滑石粉（Talc）填充聚酰亚胺（PI）复合薄膜。通过对材料的力学性能的测试与表征，初步探讨了Talc的粒径、含量、分布等因素对PI复合薄膜性能的影响。结果表明：Talc的填充可以有效改善PI复合薄膜的弹性模量，但是复合薄膜的拉伸强度和断裂拉伸应变没有改善反而会下降。Talc填充粒径为5000目20wt%时弹性模量最高。工业生产薄膜性能明显优于实验室制备试样。44070

Abstract ：Polyimide (PI) films filled with Talc were prepared by situ polymerization. And the effect of Talc particle size, mass fraction and distribution on the mechanical properties of the films was investigated. The results showed that: The introduction of the Talc can improve the elastic modulus of PI films effectively, but the tensile strength did not improve. And the film with Talc particle size 5000 mesh, and mass fraction 20wt% shows highest elastic modulus. It must be pointed out that the performance of the Talc filled polyimide film preparation in factory is much better than in labs.

毕业论文关键词：滑石粉；聚酰亚胺复合薄膜；力学性能

Keyword: Talc; PI composite films; mechanical properties

目    录

1 引言 4

2 实验部分 4

2.1实验原料 4

2.2 实验仪器、设备 4

2.3 反应原理 5

2.4 材料制备 5

2.5 性能测试 6

3结果与讨论 6

3.1 Talc含量对PI薄膜性能的影响 6

3.2 Talc分散处理方法对PI薄膜性能的影响 8

3.3 KH550界面处理对PI薄膜性能的影响 9

3.5 工业生产薄膜 9

4 结论 10

参考文献 10

致谢 11

 1 引言

聚酰亚胺（PI）有着众多优良的性能。比如力学性能、耐热性、耐溶剂性都很好，还有良好的耐辐射性，高温下良好的介电性。因为它的这些优异的综合性能，所以在电子电工和化工等行业都有广泛的应用，并且随着科技的高速发展在航天航空等领域也有广泛的应用。[1-4]

但是由于PI的工作条件特殊，所以对它的性能也有着更高的要求。比如它较差的吸水性和热膨胀性限制了它的应用。我们就需要针对特殊的需求来制备性能更加优异的PI复合材料，即改性聚酰亚胺。[5-6]

填充改性是一个很好的方法，它不仅可以保存聚酰亚胺本身的优点，也可以随着复合物的加入提高其综合性能。而且工艺简单、成本易控制，是聚合物改性最常用的方法之一。但在填充改性聚合物材料时，填充材料的均匀分散及填料与聚合物基体之间的相互作用则是制备理想性能聚合物材料的关键。本文即采用原位聚合的方制备了滑石粉（Talc）填充的聚酰亚胺复合薄膜，研究了Talc的粒径、含量、分布等因素对PI复合薄膜性能的影响。并把技术应用于实际生,产制备了Talc填充PI薄膜产品。 [7-10]

2 实验部分

 2.1实验原料

4,4’-二氨基二苯醚（ODA），上海三爱思试剂有限公司；

均苯四甲酸二酐（PMDA），溧阳龙沙化工有限公司

N,N’-二甲基甲酰胺（DMF），分析纯，上海凌峰化学试剂有限公司论文网；

滑石粉（Talc），1250目，3000目，5000目；广西龙胜华美滑石开发有限公司； 滑石粉填充聚酰亚胺薄膜性能研究:http://www.751com.cn/cailiao/lunwen_45236.html