摘要本文探讨了基础聚合物、增粘剂、溶剂等因素对溶剂型SIS胶粘剂粘接性能的影响，并利用L9（43）正交试验法分析了各因素的影响显著性。结果表明：SIS1105和1126复合使用比单一基础聚合物的粘接强度更大；增粘树脂的复配具有明显的协同作用。通过正交试验分析，萜烯树脂的影响最为显著，SIS1105次之，溶剂油和戊烷树脂影响较小。48468

Abstract Based polymer, this paper discusses the factors such as tackifier, solvent effect on the properties of solvent SIS adhesive bonding, and by using L9 (43) orthogonal test analysis of the influence of various factors of significance.The results show that the compound use SIS1105 and 1126 more than single base polymer bonding strength;Viscosity of the resin distribution has obvious synergy.Through the orthogonal experiment analysis, the influence of the terpene resin is the most significant, SIS1105 times, solvent oil and pentane resin.

毕业论文关键字：粘接性能；粘结效率指数；SIS压敏胶；正交测试

Keyword:  Peel strength；Bonding efficiency index；SIS Pressure sensitive adhesive；Orthogonal test

摘    要 3

1前言 4

1.1我国胶粘剂的发展现状 4

1.2溶剂型压敏胶 4

1.3 SIS基础聚合物的结构和性能 4

1.4 粘接性能 5

2 实验部分 5

2.1 实验原料 5

2.2实验主要仪器设备 5

2.3 实验方法 5

3  结果与讨论 6

3.1研究不同型号的基础聚合物的选择与复合对粘胶剂性质的影响 6

3.2测试不同配比的溶剂对粘胶剂性质影响 6

3.3测试不同增粘剂对性质的影响 7

3.4测试不同配比的增粘剂对性质的影响 7

3.5正交试验的安排 8

3.5.1正交试验试剂设计制备 8

3.6 实验分析 9

3.6.1 不同上胶量对粘接强度的影响 9

3.6.2不同型号的基础聚合物对粘胶剂粘接性能的影响 10

3.6.3不同比例的基础聚合物对粘胶剂粘接性能的影响 11

3.6.4不同增粘剂对粘胶剂粘接性能的影响 11

3.6.5不同增粘剂的复配对胶粘剂粘接性能的影响 12

3.6.6乙酸乙酯与溶剂油配比对粘接性能的影响 14

3.7正交测试探究对粘接性能的影响 15

3.7.1正交试验结果的分析 15

3.7.2溶剂型压敏胶的最佳配方 16

4结论与展望 16

4.1结论 16

4.2展望 16

参考文献 17

致谢 17

1前言

1.1我国胶粘剂的发展现状

  粘胶剂，在中国传统称为胶水，浆糊。粘胶剂是一种材料，这种材料可以用不同的施工工艺而做成具有不同的功能。经过几十年的发展，中国的粘胶剂产业正逐步走向成熟。过去由于大多数企业素质偏低，其盈利手段主要靠量大价低，或某一资源优势等，市场竞争也依赖中国的廉价劳动力，资源优势。然而随着经济的不断发展，迫于人力资源成本的提高，原材料价格的提升等因素，中国粘胶剂也逐步步入微利时代，被迫走向转型升级之路，形成从价格竞争转变到差异竞争，从单纯模仿走向原创创新，消费模式也由以往功能性需求向个性需求来发展，最终形成品牌竞争时代。而在我们的胶粘剂的发展过程中，溶剂型压敏胶的需求和发展都是非常快速的，因为其良好的性能和广泛的用途，所以我国各大公司都开始研制新型的溶剂型压敏胶。 溶剂型SIS压敏胶的制备及性能研究:http://www.751com.cn/cailiao/lunwen_51089.html