摘要: 本文选择了MDI/埃洛石作为沥青改性剂，通过大量实验对MDI/埃洛石改性沥青的物理力学性能、微观作用机理、相容性以及沥青混合料的路用性能作了深入研究。提出了MDI/埃洛石改性沥青混合料的配合比设计方法，为MDI/埃洛石改性沥青的应用提供理论基础。本文论述了MDI、埃洛石的矿产分布，矿物特性以及研制方法，分析了其作为沥青混合料填料与改性剂的区别。对不同掺量、不同配比的MDI/埃洛石改性沥青针入度、软化点、135 ℃布氏旋转粘度、延度四个性能指标做了研究。并根据经济分析MDI/埃洛石改性剂存在的明显综合经济效益，具有较大的推广使用价值和研究意义。48641

毕业论文关键词：改性沥青；MDI；埃洛石；结构

The performance of MDI/Halloysite composite modified asphalt

Abstract: This paper discusses the MDI/halloysite mineral distribution, mineral characteristics and research methods, analyzes its as the difference between the asphalt mixture filling and modifying agent.With different dosage, different ratio of MDI/halloysite modified asphalt penetration, softening point, 135 ℃ brinell rotary viscometer, the ductility four performance indicators to do the research, And according to the analysis of MDI/halloysite modifier exist obvious comprehensive economic efficiency, has great use value and research significance.

KeyWords: Modified asphalt,MDI,Halloysite, Structure

第一章绪论 1

1.1 沥青的组成、结构和改性基础 1

1.1.1沥青的组成 1

1.1.2沥青的结构 2

1.1.3沥青的性能表征 3

1.2沥青改性的研究 3

1.2.1非聚合物改性沥青 4

1.2.2聚合物改性沥青 4

1.2.3复合改性剂改性沥青 5

1.3 改性剂及改性原理 5

1.3.1 MDI 5

1.3.2 埃洛石 7

1.3.3改性原理 8

1.4 研究目的及意义 8

第二章 MDI改性沥青 10

2.1 MDI改性沥青的制备及表征 10

2.2 结果与讨论 10

2.2.1 软化点 10

2.2.2 粘度 11

2.2.3 针入度 12

2.2.4 延度 12

2.3 小结 13

第三章 MDI/埃洛石复合改性沥青 14

3.1 MDI/埃洛石复合改性沥青的制备及表征 14

3.2 结果与讨论 14

3.2.1 软化点 14

3.2.2 粘度 15

3.2.3 针入度 15

3.2.4 延度 16

3.3 小结 16

第四章结论与展望 17

致谢 18

参考文献 19

第一章绪论

石油沥青是原油经多级精馏之后的残渣，是由不同分子量的烃类及各种非金属衍生物组成的黑色粘稠混合物，是一种具有高粘度、高防水性的复杂有机材料。由于其优异的粘结性能和防水性能，被广泛应用于路面结构胶结材料。与不同种类的集料颗粒均匀混合后可以建成能够适应不同环境的沥青路面。但是由于石油沥青是一种粘弹性材料，它在高温下粘度较低容易流淌，而在高温和紫外线照射下却容易发生老化,低温固化后易脆裂，温度敏感性较强，所以难以满足道路的铺设要求[ ]。 MDI/埃洛石复合改性沥青性能研究:http://www.751com.cn/cailiao/lunwen_51307.html