铝合金用钎剂中粘结材料的研究

摘要：本论文采用红外光谱仪、核磁共振仪、色谱－质谱仪对铝合金钎焊用NHM-X100-20UB热分解性树脂，稀释剂进行了分析，同时进行不同的配比、通过蔡恩杯测定其粘度以及在不同温度、不同时间下测定钎剂挥发的重量，以探究热分解树脂的挥发性。仪器分析结果表明：热分解树脂的主要成分为：十八烯酰胺，十四烷酰胺，3 - 庚醇，丙烯酸类树脂。
稀释剂的主要成分为：1-甲氧基-3-甲基,丙二酸,二甲氧基丁烷。实验结果表明：稀释剂的配比越高，其粘度随稀释剂的加入量的增加而减小，其涂布之后硬度也较低，当稀释剂加入量为41.2%时，钎焊剂为最佳配比。在测试其挥发性时，相同温度下，当热分解性树脂的配比率一定时，稀释剂的配比率越高，其挥发率就越大。7755
关键词：热分解树脂；粘度；挥发性；涂层强度
Research on bonding agent for aluminum brazing materials
Abstract：This infrared spectroscopy, nuclear magnetic resonance, chromatography - mass spectrometry have been used to analyze composition of NHM-X100-20UB heat decomposable resin, diluent for aluminum alloy brazing. With a different ratio of all kinds of agent, the viscosity have been measured by Zahn cup and at different temperatures at different times of volatile flux measured weight in order to explore the thermal decomposition of volatile resin. The results of instrumental analysis showed that: the main component of the thermal decomposition of the resin: eighteen amide, myristic acid amide 3 - heptanol, an acrylic resin.The main components of the diluent: 1-methoxy-3 - methyl, malonic ,dimethoxy-butane. The experimental results showed that: the higher the ratio of the diluent, the viscosity with increase of the amount of diluent decreases, the hardness is low after coating, when the amount of diluent added was 41.2%, the brazing flux for the most good ratio. In the test the volatile, the same temperature, when the thermal decomposition of resin with the ratio constant, with the higher the ratio of diluent, the greater the evaporation rate.
Key words：Thermal decomposition of resin; viscosity; volatility; Coating strength
目录
1 前言   1
1.1 铝合金钎焊   1
1.1.1 铝合金钎焊概述   2
1.1.2铝合金钎焊的工艺方法   2
1.1.3铝合金钎焊的优缺点   3
   1.2 铝合金用钎料的分类及特点   4
1.3 铝合金用钎剂   4
1.3.1 铝合金用钎剂的分类   5
1.3.2 铝合金用钎剂的组成及作用   5
1.3.3 铝合金用钎剂的研究方向   6
1.4 铝合金用钎剂中粘结剂   7
1.4.1 粘结材料的选择原则   7
1.4.2粘结材料的应用方法   8
1.4.3 粘结材料含量对工艺性能的影响   8
1.5 选题的目的和意义   9
1.6 研究内容和目标   10
1.6.1 研究内容   10
1.6.2 研究目标   10
2 实验   11
2.1实验原材料   11
2.1.1 NHM-X100-20UB热分解性树脂   11
2.1.2 稀释剂M   11
2.1.3 苏威NOCOLOK FLUX助焊剂   11
2.1.4 WS-1架桥材   11
2.2实验设备   11
2.2.2蔡恩杯   12
2.2.3 JB50-D型增力电动搅拌机   12
2.2.3 高温加热炉   12
2.3 实验方案   12
2.3.1产品剖析   12
2.3.2钎剂配比对其粘度的影响   13
2.3.3钎剂配比对涂布量的影响   11 铝合金用钎剂中粘结材料的研究:http://www.751com.cn/cailiao/lunwen_5829.html