摘要42CrMo具有良好的综合力学性能，能够适应较差的工作环境，因此被广泛利用在风电主轴生产制造中。风电主轴的最终组织及使用性能与其工艺流程中的最后环节——调质处理密切相关，因此研究42CrMo的调质处理工艺具有重要意义。68173
采用油淬后高温回火方式对规格为Φ40mm的42CrMo钢棒材进行了调质处理，并对比分析了不同正火工艺对调质处理后钢材的微观组织和力学性能的影响。通过实验分析可知，通过660℃3h正火处理和860℃油淬加610℃回火后，显微组织均匀细小，回火索氏体的含量较高, 综合性能最好。
毕业论文关键词 42CrMo；调质；风电主轴；显微组织；力学性能
Title A typical wind power spindle quenched material properties of the
organization
Abstract
42CrMo has good mechanical properties, able to adapt to poor working environment, so it is widely used in the manufacture of wind power in the spindle. Wind power spindle final microstructure and properties of its process using the last link - quenched closely related, so the research 42CrMo quenching process is important.
By oil quenching tempering specifications for Φ40mm way of 42CrMo steel rods were quenched and comparative analysis of different quality normalizing process reversed after treatment of steel microstructure and mechanical properties. Through experimental analysis, through 660 ℃ 3h normalizing and 860 ℃ 610 ℃ oil quenching plus tempering, uniform and fine microstructure, sorbite were higher, the best overall performance.
Keywords 42CrMo; quenched; wind power main shaft; micro structure; mechanical property
目 录
1 绪论 1
1.1.1 世界风电产业发展现状 1
1.1.2 我国风电产业的发展现状 1
1．2 风电技术的发展趋势 2
1．3 42CrMO材质风电主轴在风力机中的应用 2
1.3.1 风电主轴的结构及性能要求 2
1.3.2 42CrMo钢 4
1．4 热处理技术及调质处理 4
1.4.1 我国热处理技术的发展 4
1.4.2 热处理及其种类 5
1.4.3 调质处理 7
1.4.4 钢的淬透性 7
1．5 课题的主要研究内容和思路 7
1.5.1 研究内容 7
1.5.2 研究思路 8
2 实验过程和方法 8
2．1 实验流程 8
2．2 材料准备 9
2.2.1 原材料 9
2.2.2 热处理设备 9
2.2.3 正火处理（预处理） 9
2．3 调质处理的方案设计 10
2.3.1 淬火方案的确定 10
2.3.2 回火方案的确定 典型风电主轴材料的调质处理与组织性能研究:http://www.751com.cn/cailiao/lunwen_76614.html