摘要目前，在我国一些行业中，用轻便并且总储量高的铝代替稀缺的铜已经成为一种趋势。本实验研究了三辊行星轧机轧制的ACC（一种内层为较薄的TP2铜层，外层为3003铝层的管材）的界面特征。在实验过程中使用光学显微镜观察了轧制进行到不同位置的材料的显微组织，用热分析实验检测了材料内部是否有储存能，用能谱分析检测了界面附近的元素成分及含量。研究表明，在ACC中，铜铝之间的结合方式为冶金结合，铜铝界面处有一定厚度的扩散层，轧制完成后的材料仍有一定储存能。68273

毕业论文关键词： 铜铝复合管 界面 微观结构 

毕业设计说明书（论文）外文摘要

Title The Research of Cu/Al Composite Material’s Interface    

       Characteristic

Abstract

Nowadays, in some native industries, it is a tendency to use the aluminum, which is light and of rich reserves, to replace the copper. In this research,the interfacial characteristic the ACC (Aluminum Clad Copper Tube,who’s inside is TP2 copper and outside is 3003 aluminum) produced in three roll planetary was studied. The microsturcture of different phases were observed by optical microscopy, the thermal analysis was done to make sure whether there is any storage anergy in the material, and the elemental distribution near the interface was determined by energy dispersive spectroscopy. The study showed that, in ACC, the combination mode is metallurgical bonding, there is a diffusion layer between the aluminum and copper, and some energy is still stored in the material.  

Keywords:  Aluminum Clad Copper Tube   interfacial characteristic

           microsturcture   

目次

第一章 引言 1

1.1 铜和铝材料的介绍 1

1.2 本课题的研究对象——ACC 1

1.3本课题的目的和意义 3

1.4 铜铝复合材料界面结合的研究进展 3

第二章 实验准备及实验方案 4

2.1 实验目的和方法 4

2.2 实验设备 4

2.3 实验方案 6

第三章 实验结果与分析 8

3.1 金相分析 8

3.2 热分析实验 10

3.3 能谱分析 12

3.4 实验总结 16

结论 17

致谢 17

参考文献 18

第一章 引言

1.1 铜和铝材料的介绍

铜,人类最早开始使用的金属，“具有很高的耐蚀性导热性，导电性，有优良的韧性和延展性被广泛地应用于电气，轻工，机械，建筑，国防等领域”[1]。铜在地壳中的含量仅为0.01%，目前我国纯铜的价格在每吨5.5万元以上。铝具有较高的导热性，导电性和耐蚀性，有优异的加工性能。铝在地壳中含量为8.2%，仅次于氧和硅，目前我国纯铝的价格在每吨1.5万元左右。铝虽然在一些性能上略逊于铜，但是储量高，价格便宜，而且密度小，因此常作为铜的替代品，被称为“以铝节铜”[2~6]。

                           表1 铜铝各方面指标对比 Cu/Al复合材料界面组织特征研究:http://www.751com.cn/cailiao/lunwen_76757.html