摘要：本论文通过选择了不同的反应性乳化剂制备了水性酮肼交联树脂、N-羟甲基丙烯酰胺交联树脂、环氧交联树脂。测定了各类水性树脂的性能，同时研究了环氧交联体系在常温、80℃及120℃下固化成膜和N-羟甲基丙烯酰胺在80℃和120℃下固化成膜的性能，并进行红外表征。结果表明，三种交联体系中，水性酮肼交联体系适用于水性木器漆的生产；N-羟甲基丙烯酰胺交联丙烯酸酯体系适用于水性皮革涂饰剂的生产；水性环氧交联丙烯酸酯体系适用于水性防腐漆的生产。9104
关键字：功能水性丙烯酸树脂;性能；应用；水性木器漆；水性防腐漆；水性皮革涂饰剂
Applied Research of Functional Waterborne Acrylic Resin
Abstract：In this paper, by choosing different reactive emulsifier to complete the preparation of Waterborne Ketone hydrazine crosslinked resin,N-methylol acrylamide crosslinkedresin,Crosslinked epoxy resins. Measured the performance of various types of water-based resin Also studied the film performance of the epoxy crosslinking system at room temperature, 80 ℃ and 120 ℃ and the N-methylol acrylamide and 120 ℃ at 80 ℃，and characterized by its infrared.The results show that,in three kinds of cross-linking system,the aqueous ketone hydrazine crosslinking system for waterborne wood production; N-methylol acrylamide crosslinked acrylate system for the production of water-based leather finishes; waterborne epoxy crosslinked acrylate system for the production of water-based anticorrosive paint.
Keywords: Functional aqueous acrylic resin; Performance;Application; Waterborne Wood Coatings; Water-based anti-corrosion paint; Water-based leather finishes
目录
1绪论 1
1.1水性酮肼交联概述 1
1.2水性N-羟甲基丙烯酰胺交联丙烯酸酯概述 3
1.3水性环氧交联丙烯酸酯概述 3
1.4水性木器漆概述 4
1.5皮革涂饰剂概述 5
1.6水性防腐涂料概述 6
2试验 6
2.1原料名称、规格和来源 6
2.2水性体系交联机理 7
2.2.1水性酮肼交联体系反应机理 7
2.2.2水性N-羟甲基丙烯酰胺交联丙烯酸酯体系反应机理 7
2.2.3水性环氧交联丙烯酸酯体系反应机理 7
2.3水性体系基本反应 8
2.3.1水性酮肼交联反应 8
2.3.2水性N-羟甲基丙烯酰胺交联体系反应 11
2.3.3水性环氧交联丙烯酸酯体系反应 12
2.4水性树脂合成方法 13
2.4.1水性酮肼交联树脂制备合成方法 13
2.4.2水性N-羟甲基丙烯酰胺树脂合成方法 13
2.4.3水性环氧交联丙烯酸树脂合成方法 14
2.5性能测试 14
2.5.1固含量的测定 14
2.5.2吸水率的测定 14
2.5.3红外测试 15
2.5.4耐乙醇、耐碱、耐酸、耐水性（浸泡法） 15
2.5.5干燥时间的测定 15
2.5.6粘度的测定 15
2.5.7光泽度的测定 15
2.5.8铅笔硬度 16
2.5.9耐盐水性 16
2.5.10耐磨性 16
3结果与讨论 17
3.1水性树脂体系的应用选择 17
3.2水性酮肼交联丙烯酸酯体系的性能研究 18
3.2.1水性酮肼交联树脂结构的红外表征 18
3.2.2水性酮肼交联丙烯酸酯乳液的性能指标 19 功能水性丙烯酸树脂的应用研究:http://www.751com.cn/cailiao/lunwen_7706.html