锆酸镧陶瓷粉的制备+文献综述(8)

时间:2017-01-05 15:26来源:毕业论文
图3.2不同反应时间产物的XRD图 图3.2是不同反应时间产物的XRD图,从图3.2中可知在反应物与熔融盐比为1:2、反应温度为1000℃、分别在1h、2h、3h、4h、5h、8h、


 
图3.2不同反应时间产物的XRD图
图3.2是不同反应时间产物的XRD图,从图3.2中可知在反应物与熔融盐比为1:2、反应温度为1000℃、分别在1h、2h、3h、4h、5h、8h、9h、10h所得产物中除La2Zr2O7
 

表3.1不同反应时间产物的数据表
hkl    标准    1h    2h    3h    4h    5h    8h    9h    10h
ZrO2(001)    17.483    17.51172    17.49500413    17.5117154    17.5117154    17.49500413    17.49500413    17.47829286    17.49500413
ZrO2(110)    24.072    24.21293    24.12937792    24.07924411    24.12937792    24.07924411    24.14608919    24.12937792    24.06253284
ZrO2(011)    24.472    24.59729    24.5137371    24.74769487    24.48031457    24.58058218    24.49702583    24.5137371    24.48031457
ZrO2(-111)    28.214    28.37404024    28.29048389    28.29048389    28.30719516    28.35732897    28.30719516    28.32390643    28.24035009
ZrO2(111)    31.492    31.61602642    31.53247007    31.56589261    31.54918134    31.58260388    31.51575881    31.58260388    31.465625
ZrO2(200)    34.197    34.28982946    34.22298438    34.23969565    34.22298438    34.27311819    34.18956184    34.22298438    34.1561393
ZrO2(020)    34.401    34.50707595    34.44023088    34.47365341    34.45694215    34.40680834    34.44023088        
ZrO2(002)    35.335    35.35935067    35.39277321    35.40948448    35.40948448    35.42619575    35.35935067    35.35935067    35.3426394
ZrO2(-201)    35.922    35.91082255    35.94424508    35.92753382    35.91082255        35.94424508        
ZrO2(120)    38.589    38.60133685    38.65147066    38.61804812    38.61804812        38.60133685        
ZrO2(012)    39.474    39.50374538    39.4369003    39.47032284    39.45361157    39.48703411    39.45361157    39.48703411    39.48703411
ZrO2(-112)    40.765    40.90749197    40.82393563    40.75709055    40.80722436    40.8406469    40.79051309    40.79051309    40.79051309
ZrO2(201)    41.213    41.24171735    41.22500608    41.20829481    41.22500608                 锆酸镧陶瓷粉的制备+文献综述(8):http://www.751com.cn/huaxue/lunwen_1876.html