5A06高强铝镁合金新型双脉冲焊接工艺方法研究

菜单

摘要针对30mm厚的高强5A06铝镁合金板，应用双脉冲MIG焊接工艺，进行堆焊和对接焊接工艺试验研究，并对获得的焊缝进行了外观检查，并进一步对焊接接头微观组织进行分析，对焊接缺陷产生的原因进行了详细的分析。试验结果表明，当低频频率为3Hz时，采用双V型对称坡口，双面分别进行3层6道对称焊接方式，可以获得表面成型美观的缝成型。同时发现当根部清根不足时，厚板对接接头根部容易出现局部未熔合；当侧壁焊接时焊接位置距离侧壁和前道焊缝较远时，容易侧壁存在少量未熔合和层间未熔合缺陷。67695

毕业论文关键词 5A06铝合金双脉冲MIG焊接参数微观组织

毕业设计说明书（论文）外文摘要

Title The Research on weldingprocesstechnologyof high-strength aluminum-magnesium alloy

Abstract

The main topic for 30mm thick 5A06 aluminum alloy sheet，Conduct the surfacing welding process testing, and the docking welding with the double pulse MIG welding. To the welding joints, the weld appearance inspection. Then, conduct the t microstructure analysis and explain the reason of weld defects. The results show that, when frequency is 3Hz, double v-shaped symmetrical groove, double-sided respectively 3 layer 6 symmetry welding way, can obtain surface shape and beautiful seam. Also found that when the lack of clear root, prone to local plate butt joint root incomplete fusion; When distance side wall welding when the welding location and former welding seam is far, easy wall there is a small amount of incomplete fusion and incomplete fusion defects between the layers

Keywords 5A06aluminum alloy Double pulse MIG Welding parameter microstructure

1 绪论 2

1.1 选题背景与选题意义 2

1.2高强铝合金焊接技术研究现状 2

1.3双脉冲MIG焊的研究现状 4

1.4 本课题研究内容 5

2 试验材料和设备 6

2.1 试验材料 6

2.2 试验设备 6

2.3焊接方法 8

2.4 焊接过程 9

2.5 金相组织分析流程 10

3 高强铝镁合金堆焊焊接工艺试验研究 10

3.1 焊接规范 10

3.2焊接外观成型 11

4 高强铝镁合金对接焊接工艺试验研究 14

4.1坡口形式 14

4.2 焊接规范 15

4.3焊接接头的宏微观组织 16

4.4焊接接头缺陷分析 22

4.5焊接变形量分析 24

4.6焊接接头显微硬度 25

结论 27

致谢 28

参考文献 29

1 绪论

1.1 选题背景与选题意义

铝及铝合金的比强度及导电导热性比较高，同时它还具有较高的热容量和熔化潜热,耐腐蚀性以及低温下的机械性能都比较好，因此,铝合金是有色金属结构材料在工业中应用最广泛的一类，在航天、航空、机械制造、汽车、船舶及化学工业中已大量应用,也正因为铝合金的广泛应用，铝合金焊接技术得到了很大的发展，同时焊接技术的发展也拓展了铝合金的应用领域[1]。因此，如何解决铝合金的焊接问题正成为现今焊接技术研究的热点之一。各种各样的焊接方法也被运用到铝合金焊接中，如TIG焊、MIG焊、激光-电弧复合焊、搅拌摩擦焊等。这些焊接方法各有优势与不足，适用于不同的行业领域。论文网