    摘要本文采用化学还原法制备石墨烯薄片,采用双脉冲复合电沉积法制备镍基石 墨烯复合镀层,同时研究镀液中石墨烯浓度对复合镀层的力学性能与摩擦磨损性 能的影响。经过 SEM,TEM,EDS,XRD,Raman 和 FT-IR 等技术分析后发现:改进 Hummers 法结合肼还原法可以获得质量较好的石墨烯,用电沉积法可以获得镍基 石墨烯复合镀层,而复合镀层中的确存在石墨烯。同时还利用电沉积法制备了镍 基金刚石复合镀层,镍基碳纳米管复合镀层进行比较。石墨烯对于复合镀层的硬 度提高和摩擦系数的降低起到一定的作用,随着石墨烯添加量的增加,硬度和减 摩润滑效果也随之提高。当石墨烯添加量过多时,不利于复合镀层的制备,对力 学性能和摩擦学性能也不好。68569

    毕业论文关键词 :石墨烯 氧化还原法 改进 Hummers 法 自润滑 摩擦磨损性能

    Title Research on Graphene Preparation by RODEX and   Its Influence on the Tribological Performance of Nickel-based coating

     

     

    Abstract

     

    In this paper ,chemical method was used to prepare the graphene sheets and double pulse electrodeposition process was used to prepare the graphene

    /nickel based composite coatings. Furthermore, the influence of graphene concentration on mechanical properties and friction and wear performance was discussed.By SEM, TEM, EDS, XRD , Raman spectra and FT-IR, it was found that: through improved hummers method with the hydrazine reduction method ,the graphene with quite good quality can be prepared.

    The graphene /nickel based composite coatings could be prepared successfully by the double pulse electrodeposition process. And graphene exists in the composite coatings indeed. We also prepared nickel-based diamond composite coating, nickel-based carbon nanotube composite coatings for comparison in the same way . Graphene played a role in increasing the hardness and decrease of friction coefficient,. With the increase of grapheme amount, the hardness and lubricity of composite coatings were also improved. When the amount of graphene was superfluous, it was detrimental to the preparation of composite coatings , the mechanical property and tribological performance.

     

     

    Keywords graphene RODEX improved hummers method Self lubricating friction and wear 

    1 引言 1

    1.1 自润滑及复合镀层摩擦性能概述 1

    1.2 石墨烯概述 2

    1.2.1 石墨烯的性质及石墨烯复合材料 2

    1.2.2 石墨烯的制备 3

    1.2.3 石墨烯摩擦性能及石墨烯复合镀层耐磨性 3

    1.3 研究目的和研究内容 4

    2 实验条件和方法 6

    2.1 主要实验流程

  1. 上一篇:硫化物二维半导体阻变存储器设计
  2. 下一篇:铁尾矿烧结陶粒的制备工艺XRD分析
  1. 甘氨酸燃烧合成法抗Cr毒化...

  2. 溶胶—凝胶法制备多晶钇铝石榴石纤维制备

  3. ANSYS铝棒挤压成形有限元法数值模拟

  4. 相场法研究铝浓度对镍铝...

  5. 硬模板法制备纳米级二氧...

  6. 氧化锆纤维板的成型工艺及对其性能影响研究

  7. 基于遗传算法与神经网络...

  8. 当代大学生慈善意识研究+文献综述

  9. 酸性水汽提装置总汽提塔设计+CAD图纸

  10. 河岸冲刷和泥沙淤积的监测国内外研究现状

  11. 电站锅炉暖风器设计任务书

  12. 乳业同业并购式全产业链...

  13. java+mysql车辆管理系统的设计+源代码

  14. 大众媒体对公共政策制定的影响

  15. 十二层带中心支撑钢结构...

  16. 杂拟谷盗体内共生菌沃尔...

  17. 中考体育项目与体育教学合理结合的研究

  

About

751论文网手机版...

主页:http://www.751com.cn

关闭返回