摘要：本课题主要内容：制备一种预膜剂。主要成分为聚磷酸盐和表面活性剂。改变各成分浓度，评定预膜效果，筛选最佳方案。本课题中所研制的预膜剂主要成分聚磷酸盐和表面活性剂。常用的是751偏磷酸钠和三聚磷酸钠。本文采用以聚磷酸盐为主的磷- 锌系列预膜剂,加以表面活性剂，利用其高效的润湿、分散、增溶等作用, 来使相关离子失粘、细化并均匀分散在水中，从而提高预膜性能。并且通过肉眼观察情况和点滴实验来讨论各种方案的预膜效果。23920
- 上一篇：苯基乙烯基硅树脂的制备与性能分析
- 下一篇：以SiO2空心球为壁材的微胶囊香精制备
根据实验结果，最佳预膜方案为：三聚磷酸钠浓度60mg/L；氯化钙浓度：100 mg/L;硫酸锌浓度：50 mg/L；乳化剂op-10：40mg/L。CuSO4点滴试验红点析出平均时间为57.21s。
毕业论文关键词：预膜剂；聚磷酸盐；表面活性剂
Development of Surfactant-Polyphosphate prefilming agent
Abstract: In this thesis, we focus on development of surfactant-polyphosphate prefilming agent and further study the performance of the prefilming agent.
Based on the fact that Prefilming agent can produce protective film on the surface of metal. It is an effective method to prevent circulating cooling water system from corrosion after acid cleaning. We adopt phosphorous- zinc series prefilming agent with surfactant. By means of corrosion tests, we discuss performance of each prefilming scheme by observing and carrying out droping experiment.
The results showed that the best option of prefilming design is phosphate:60mg/L、op-10=40mg/L 、Zn2+ =50mg/L、Ca2+= 100mg/L、48h in constant temperature.
Key words: Prefilming agent; Polyphosphate; Surfactant
目 录
1 绪论•1
1.1 课题研究背景1
1.2 预膜剂的现状2
1.3 课题综述3
1.3.1 预膜剂的预膜机理3
1.3.2 预膜剂的分类•3
1.3.3 表面活性剂的定义•4
1.3.4 表面活性剂的分类4
1.3.5 表面活性剂在预膜中的作用 •5
1.4 常用预膜剂的研究•5
1.4.1 聚磷酸盐-锌盐预膜剂-••5
1.4.2 有机膦酸盐预膜剂5
1.4.3 低磷预膜剂5
1.4.4 表面活性剂预膜剂5
1.5 本论文研究的内容6
2 实验部分•8
2.1 实验仪器与药品8
2.1.1 主要原料•9
2.1.2 主要仪器设备•9
2.2 聚磷酸盐预膜剂的制备9
2.2.1 试剂9
2.2.2 聚磷酸盐筛选试验•10
2.2.3 确定最佳钙离子浓度•10
2.2.4 确定最佳锌离子浓度10
2.2.4 表面活性剂筛选试验••10
2.3 预膜效果评定•• 10
3 结果与讨论11
3.1 聚磷酸盐预膜剂的制备••11
3.1.1 聚磷酸盐筛选试验••11
3.1.2确定最佳钙离子浓度••14
3.1.3 确定最佳锌离子浓度16
3.1.4 表面活性剂筛选试验••16
3.2 影响预膜效果因素••20
3.2.1 温度20
3.2.2 时间20
4 结论21
致谢 22
参考文献 23
1 绪论
1.1 课题研究背景
清洗和预膜称为循环冷却水系统化学处理的预处理。清洗，对新系统可以清除循环冷却系统内的杂质和金属腐蚀物，提高预膜效果，减少腐蚀和结垢的产生；对老系统，可提高换热效率，改善工艺条件，保证长的生产周期，降低能耗和延长设备使用寿命。预膜是为了提高缓蚀剂的成膜效果，常在循环水开车初期投加较高的缓蚀剂量，待成膜后，再降低药剂浓度文持补膜即所谓的正常处理。这种预膜处理，其目的是希望在金属表面上很快形成一层保护膜，提高缓蚀剂抑制腐蚀的效果。