摘要本文主要研究在三酚基甲烷型环氧树脂合成的过程中抑制分子链之间的反应，从而实现降低三酚基甲烷型环氧树脂粘度的目的。以三酚基甲烷单体与环氧氯丙烷缩合反应合成低粘度三酚基甲烷型环氧树脂,采用正交实验的方法，开展工艺条件的优化研究，并对三酚基甲烷型环氧树脂的提纯方法进行研究。通过不同反应条件的对比，得出优质低粘度三酚基甲烷型环氧树脂的最佳工艺条件。并研究TMP/MNA固化体系的固化动力学过程，得到动力学参数和最佳固化工艺。27655
- 上一篇：二甲基二烯丙基氯化铵中烯丙基类杂质形成机理初探
- 下一篇：Knoevenagel反应新型硝基二苯乙烯类化合物的设计与合成
关键词：三酚基甲烷 环氧树脂 低粘度 热固性树脂
毕业论文设计说明书外文摘要
Title The Preparation of Triphenyl Glycidyl Ether Methane Epoxy Resin with Low Viscosity
Abstract
In this paper, we mainly research in triphenyl glycidyl ether methane in the process of the epoxy resin synthesis inhibition reaction between molecular chains, so as to realize triphenyl glycidyl ether methane to reduce its epoxy resin viscosity. With triphenyl glycidyl ether methane monomer and epoxy chloropropane condensation reaction synthesis triphenyl glycidyl ether methane type epoxy resin, low viscosity with the method of orthogonal experiment, study on the optimization of process conditions, and the triphenyl glycidyl ether methane purification method of the epoxy resin were studied. Compared by different reaction conditions, it gives the best preparation condition of high quality and low viscosity three phenol methane type epoxy resin. Probing the curing system of TMP / MNA curing kinetics, determining the parameters and curing process.
Key words: triphenyl glycidyl ether methane; epoxy resin; low viscosity; thermosetting resin
目 次
1 引言 1
1.1 研究背景 1
1.2 环氧树脂的分类 1
1.2.1 缩水甘油醚型环氧树脂 2
1.2.2 缩水甘油酯型环氧树脂 2
1.2.3 缩水甘油胺型环氧树脂 2
1.3 低粘度环氧树脂的研究进展 3
1.3.1 新型低粘度环氧树脂的研究进展 3
1.3.2 低粘度环氧树脂固化剂的研究进展 4
1.4 三酚基甲烷及其环氧树脂的合成研究进展 5
1.4.1 三酚基甲烷的合成 5
1.4.2 三酚基甲烷型环氧树脂的合成 6
1.5 本论文的主要研究工作 6
2 三酚基甲烷型环氧树脂的合成与表征 8
2.1 三酚基甲烷型环氧树脂的合成 8
2.1.1 实验原料及仪器 8
2.1.2 实验步骤 8
2.2 三酚基甲烷型环氧树脂的合成及其工艺优化（正交实验） 9
2.3 三酚基甲烷型环氧树脂的提纯精制 11
2.4 三酚基甲烷型环氧树脂的表征 11
2.4.1 红外光谱分析 11
2.4.2 核磁谱图分析 11
2.5 本章小结 12
3 TMA/MNA体系固化动力学研究 13
3.1 TMP/MNA体系固化动力学参数 13
3.2 TMP/MNA体系固化工艺 15
3.3 本章小结 15
结 论 17
致 谢 18
参考文献19
表格 1实验试剂 8
表格 2实验仪器 8