摘要本文选择了硝酸胍/硝酸钡复合体系做氧化剂、硼粉做可燃剂，根据烟火药配方设计理论设计了一系列点火药。通过燃速的测定，优选出一种快速点火药；使用热分析，确定以Fe2O3为增速剂，进一步提高了点火药的燃烧性能；利用透过率和感度试验表征了其微烟和安全特性，并成功制备出微烟引火线，测定了引线的燃烧速度。结果表明：当硝酸胍/硝酸钡/硼粉=55/30/15，且外加3%氧化铁时，微烟引线燃烧线速度达到0.95cm/s，烟雾量较黑火药降低72.1%，感度比黑火药低。28429
- 上一篇：基于纳米团簇探针的电致发光核酸分子诊断
- 下一篇：粉状PDMDAAC制备工艺条件的初探
关键词 点火药 微烟 热分析 感度 硝酸胍
毕业论文设计说明书外文摘要
Title Research of smokeless safety ignition composition and applied in the ignition wire
Abstract
The smokeless safety ignition composition is designed by use guanidine nitrate and barium nitrate complexes as oxidizer,boron powder as combustibles,iron(III) oxide as addenda which is used to increase the combustion speed.Using the thermal analysis equipment to determine iron(III) oxide as accelerators. Research on the combustion performance , smoke and sensitivity density through the experiment of burning rate,the concentration of smoke and the experiment of sensitivity .Then prepared the formula into ignition wire to test.The results show that: when guanidine nitrate/barium nitrate/boron = 55/30/15 and add 3% iron(III) oxide extra,the combustion speed of the line 0.95 cm/s, the ratio of black powder which produces smoke reduction of 72.1%,sensitivity lower than black powder.
Keywords ignition composition smokeless thermal analysis sensitivity guanidine nitrate
目 次
1 绪论 1
1.1 研究背景和意义 1
1.2 国内外研究现状 1
1.3 本课题研究的目标 2
1.4 本课题拟解决的关键问题 3
2 微烟安全点火药药剂配方设计基本原理 4
2.1微烟安全点火药剂组分选择 4
2.1.1氧化剂的选择 4
2.1.2可燃剂的选择 4
2.1.3添加剂的选择 5
2.1.4氧平衡计算 5
2.2烟火药的燃烧速度 6
2.3提高烟火药燃速的有效途径 6
2.3.1影响燃速的因素 6
2.3.2提高燃速的途径 6
2.4烟量的测定 7
2.5感度的测定 7
2.5.1撞击感度的测定 7
2.5.2摩擦感度的测定 8
2.6烟火药剂制备工艺 9
2.6.1成分的准备 9
2.6.2 烟火药的制备工艺流程 10
3.烟火药剂微烟安全化的研究与性能测试 11
3.1原材料的选择 11
3.1.1原材料选择的依据 11
3.1.2选定原材料 11
3.2配方设计 11
3.2.1烟雾来源 11
3.2.2配方优选 11
3.2.3实验器材 12
3.2.4试验方法 13
3.2.5实验结果与分析 13
3.3引线制作与燃速测试 13
3.3.1引线制作 13
3.3.2实验测试及结果分析 15
3.4添加剂对烟火药燃速的影响 15
3.4.1加入添加剂的配方 15
3.4.2热分析 16
3.4.3添加剂的含量对烟火药放热的影响 18
3.4.4 改进配方测燃速 19